- Product Details
- {{item.text}}
Quick Details
-
Place of Origin:
-
Shandong, China
-
Brand Name:
-
Tisco
-
Model Number:
-
ENiFe-Cl, ENiFe-Cl
-
Operating Current:
-
none, AC DC
-
Application:
-
cast iron welding
-
Usages:
-
cast iron welding
-
Keyword:
-
Cast iron welding rod
-
MOQ:
-
500 kgs
-
Packing:
-
1kg/box, 10kg/carton
-
Advantage:
-
Excellent Welding Performance
-
Color:
-
Black
Quick Details
-
Material:
-
NiFe
-
Welding Current:
-
90-190
-
Operating Temperature:
-
normal temperature
-
Place of Origin:
-
Shandong, China
-
Brand Name:
-
Tisco
-
Model Number:
-
ENiFe-Cl, ENiFe-Cl
-
Operating Current:
-
none, AC DC
-
Application:
-
cast iron welding
-
Usages:
-
cast iron welding
-
Keyword:
-
Cast iron welding rod
-
MOQ:
-
500 kgs
-
Packing:
-
1kg/box, 10kg/carton
-
Advantage:
-
Excellent Welding Performance
-
Color:
-
Black
CHARACTERISTICS:
THZ408 is the cast iron electrode with nickel iron alloy core and strong reduction of graphite coating . It can be used in AC and DC dual purpose, has stable arc,and is easy to operate. The electrode has the characteristics of high strength, good plasticity, low linear expansion coefficient and so on. The crack resistance for grey cast iron is as much as that for THZ308, while the crack resistance for nodular cast iron is more than THZ308. For cast iron with higher phosphorus (0.2%P), it also has a good results and its tocutting performance is lower than THZ308 and THZ508 slightly. THZ408 is used in the welding of gray iron and nodular cast iron for room
THZ408 is the cast iron electrode with nickel iron alloy core and strong reduction of graphite coating . It can be used in AC and DC dual purpose, has stable arc,and is easy to operate. The electrode has the characteristics of high strength, good plasticity, low linear expansion coefficient and so on. The crack resistance for grey cast iron is as much as that for THZ308, while the crack resistance for nodular cast iron is more than THZ308. For cast iron with higher phosphorus (0.2%P), it also has a good results and its tocutting performance is lower than THZ308 and THZ508 slightly. THZ408 is used in the welding of gray iron and nodular cast iron for room
Product Paramenters
|
Warranty
|
3 years
|
|
Customized support
|
OEM, ODM
|
|
Place of Origin
|
China
|
|
Model Number
|
E316L-16 CHS022 /CHS042 E309LMo-16
|
|
Operating Current
|
DCEP or AC
|
|
Welding Current
|
International standard
|
|
Operating Temperature
|
Standard temperature
|
|
Application
|
Structural steel
|
|
ISO 9001
|
Approved
|
|
in stock
|
Spot sales
|
Product Advantage
Product Application
ATTENTION:
Precautions:
1 Before welding, the electrodes need to be baked for 1 hour with the temperature of 150±10℃ before using.
2. When welding ,it is appropriate to take narrow weld and each weld length should not exceed 50mm. Hammer the welding area lightly with a hammer immediately after welding in order to eliminate stress and prevent cracks. Chemical Composition of the deposited metal(the mass fraction): %
Precautions:
1 Before welding, the electrodes need to be baked for 1 hour with the temperature of 150±10℃ before using.
2. When welding ,it is appropriate to take narrow weld and each weld length should not exceed 50mm. Hammer the welding area lightly with a hammer immediately after welding in order to eliminate stress and prevent cracks. Chemical Composition of the deposited metal(the mass fraction): %
|
Elements
|
C
|
Si
|
Mn
|
S
|
Fe
|
Ni
|
Cu
|
The mass of other elements
|
|
Standard value
|
0.35-0.55
|
≤0.75
|
≤
2.3 |
≤0.025
|
3.0-
6.0 |
60-
70 |
25-
35 |
≤
1.0 |
Welding reference current:(AC,DC+)
|
Electrode diameter(mm)
|
3.2
|
4.0
|
5.0
|
|
Welding current(A)
|
90-110
|
120-150
|
160-190
|
APPLICATIONS:
Some of our products have been applied to overseas key projects.
Electrode, SAW wire and flux of 600MPa Grade & 800MPa Grade applied to hydro steel at Laos pumped storage power station E6010 cellulose electrode Applied to the Ghana TEMA pipeline project in Africa successfully. It breaks the monopoly of Bohler cellulose electrode and won the bidding of oil pipeline Ghana tank project
Some of our products have been applied to overseas key projects.
Electrode, SAW wire and flux of 600MPa Grade & 800MPa Grade applied to hydro steel at Laos pumped storage power station E6010 cellulose electrode Applied to the Ghana TEMA pipeline project in Africa successfully. It breaks the monopoly of Bohler cellulose electrode and won the bidding of oil pipeline Ghana tank project
Hot Searches