- Product Details
- {{item.text}}
Quick Details
-
Model Number:
-
HDPE P6006AD
-
Package:
-
25kg/bag
-
Color:
-
black
-
Material:
-
HDPE Clear Pellets
-
Sample:
-
available
Quick Details
-
color:
-
black
-
Shape:
-
Pellets
-
Place of Origin:
-
Saudi Arabia
-
Model Number:
-
HDPE P6006AD
-
Package:
-
25kg/bag
-
Color:
-
black
-
Material:
-
HDPE Clear Pellets
-
Sample:
-
available
|
Physical Properties
|
Metric
|
|
English
|
Comments
|
|
|
Density
|
0.959 g/cc
|
|
0.0346 lb/in³
|
ASTM D1505
|
|
|
Oxidative Induction Time (OIT)
|
>= 30 min
@Temperature 210 °C |
|
>= 30 min
@Temperature 410 °F |
EN 728
|
|
|
Carbon Black Loading
|
2.25 %
|
|
2.25 %
|
ISO 6964
|
|
|
Melt Flow
|
0.23 g/10 min
@Load 5.00 kg, Temperature 190 °C |
|
0.23 g/10 min
@Load 11.0 lb, Temperature 374 °F |
ISO 1133
|
|
|
|
6.4 g/10 min
@Load 21.6 kg, Temperature 190 °C |
|
6.4 g/10 min
@Load 47.6 lb, Temperature 374 °F |
ISO 1133
|
|
|
Mechanical Properties
|
Metric
|
English
|
|
Comments
|
|
|
Tensile Strength, Yield
|
23.0 MPa
|
3340 psi
|
|
Test specimen according to ISO 527-2 type 1 BA, thickness 2mm with 50mm/min test speed.; ASTM D638
|
|
|
Elongation at Break
|
>= 350 %
|
>= 350 %
|
|
Test specimen according to ISO 527-2 type 1 BA, thickness 2mm with 50mm/min test speed.; ISO 527
|
|
|
Tensile Modulus
|
0.900 GPa
|
131 ksi
|
|
Test specimen according to ISO 527-2 type 1 BA, thickness 2mm with 50mm/min test speed.; ASTM D638
|
|
|
Charpy Impact, Notched
|
2.60 J/cm²
|
12.4 ft-lb/in²
|
|
Based on compression molded sheet; ISO 179
|
|
|
Tensile Creep Modulus, 1000 hours
|
360 MPa
|
52200 psi
|
|
100HR; Based on compression molded sheet; ISO 527-2
|
|