Light viscosity and good flowability RTV2 liquid silicone rubber cast silicon mold liquid rubber silicon

Light viscosity and good flowability RTV2 liquid silicone rubber cast silicon mold liquid rubber silicon

FOB Reference Price: Get Latest Price

≥100 Kilograms

US $6.3

≥2000 Kilograms

US $5.8

≥60000 Kilograms

US $5.2

Free Inquiry

Customized Request

Product Details

{{item.text}}

Quick Details

Color:: Translucent

Features:: High Temperature Resistant

Appearance:: Liquid Two Component

Usage:: Insulate Product

Certificate:: MSDS

Mixing ratio:: 100:3

Sample service:: Sample Test

Hardness:: Shore 0-60A

Quick Details

Place of Origin:: Huizhou

Brand Name:: Jiajing Hong Silicone

Product name:: Raw Material Silicone Rubber

Color:: Translucent

Features:: High Temperature Resistant

Appearance:: Liquid Two Component

Usage:: Insulate Product

Certificate:: MSDS

Mixing ratio:: 100:3

Sample service:: Sample Test

Hardness:: Shore 0-60A

Products Description

Condensation mold silicone

Condensation mold silicone is a kind of condensed liquid silica gel, component A is a liquid, component B is a curing agent, the
two materials are mixed at a ratio of 100:2 or 3 and mixed well to quickly turn liquid silica gel into solid silica gel, easy to
operate.

Product Usage

* Mold making for gypsum, GRC (glass fiber reinforced cement), cement, resin, and other products.

* Artificial stone molding, wax casting process

* Mold making for architectural decoration and other products (such as cornices, fireplaces, wall decoration, planting vessels, European furniture, decoration, etc.)

* Unsaturated resin crafts, epoxy resin crafts, poly resin crafts, polyester resin mold making.

* Handcrafted soap and candle crafts, stationery gifts and other handicraft industries.

* Casting statues, Buddha statues, Christmas ornaments, figures and other mold making.

* Customized product

Product Paramenters

Model	610	615	620	625	630	640	650	660
Appearance	White	White	White	White	White	White	White	White
Hardness (Shore Aº)	10±2	15±2	20±2	25±2	30±2	40±2	50±2	60±2
Mixing weight ratio of two components (A:B)	100: 2/3	100: 2/3	100:3	100:3	100:3	100:3	100:3	100: 2/3
Dynamic viscosity (mPa.s)	9600±2000	12000±2000	18000±2000	23000±2000	25000±2000	12000±2000	30000±2000	32000±2000
Tensile strength (MPa)	3.2	3.2	4.2	4.5	4.5	4.2	2.8	2.6
Tear strength(kN/m)	12±2	16±2	20±2	27±2	25±2	23±2	12±2	10±2
Elongation(%)	320	389	440	550	560	580	180	160
Density(g/cm)	1	1.05	1.05	1.12	1.13	1.14	1.16	1.18
Operation time(min)	30-60	30-60	30-60	30-60	30-60	30-60	30-60	30-60
Vulcanization time (h)	4-6	4-6	4-6	4-6	4-6	4-6	4-6	4-6
Line shrinkage not rate (%)	≤0.1	≤0.1	≤0.1	≤0.1	≤0.1	≤0.1	≤0.1	≤0.1

Model	510	515	520	525	530	540	550	560
Appearance	White	White	White	White	White	White	White	White
Hardness (Shore Aº)	10±2	15±2	20±2	25±2	30±2	40±2	50±2	60±2
Mixing weight ratio of two components (A:B)	100: 2/3	100: 2/3	100:3	100:3	100:3	100:3	100:3	100: 2/3
Dynamic viscosity (mPa.s)	9600±2000	12000±2000	15000±2000	25000±2000	27000±2000	15000±2000	30000±2000	30000±2000
Tensile strength (MPa)	2.4	2.8	3.7	4.5	4.2	3.6	2.4	2.2
Tear strength(kN/m)	10±2	12±2	14±2	16±2	18±2	16±2	12±2	10±2
Elongation(%)	260	320	320	350	360	320	140	120
Density(g/cm)	1	1.05	1.05	1.12	1.13	1.14	1.16	1.18
Operation time(min)	30-60	30-60	30-60	30-60	30-60	30-60	30-60	30-60
Vulcanization time (h)	4-6	4-6	4-6	4-6	4-6	4-6	4-6	4-6
Line shrinkage not rate (%)	≤0.1	≤0.1	≤0.1	≤0.1	≤0.1	≤0.1	≤0.1	≤0.1