- Product Details
- {{item.text}}
Quick Details
-
Model Number:
-
LC-1512
-
purpose:
-
each kind of paper varnishing
-
main raw material:
-
Acrylic emulsion
-
appearance:
-
milky white liquid
-
application:
-
in-line printing machine with coating or off-line glazing
-
fearure:
-
high gloss with good wearing resistance
-
Shelf time:
-
12 Monthhs
-
drying method:
-
IR or hot air
-
printing process:
-
postpress finishing
-
MF:
-
mixture
-
gloss degree:
-
80±3°
Quick Details
-
Printing Type:
-
Offset printing
-
Place of Origin:
-
Guangdong, China
-
Brand Name:
-
LCCX
-
Model Number:
-
LC-1512
-
purpose:
-
each kind of paper varnishing
-
main raw material:
-
Acrylic emulsion
-
appearance:
-
milky white liquid
-
application:
-
in-line printing machine with coating or off-line glazing
-
fearure:
-
high gloss with good wearing resistance
-
Shelf time:
-
12 Monthhs
-
drying method:
-
IR or hot air
-
printing process:
-
postpress finishing
-
MF:
-
mixture
-
gloss degree:
-
80±3°
water-based gloss finished high gloss bright varnish for print sheet paper varnishing high gloss Offset roller water based varnish LC-1512
LC-1512 is a modified acrylic polymer emulsion, is specially designed for paper printing glazing or coating requirements of products, through roller coating and after fully drying can improve the printing quality of the gloss, increase the printing products’ wear resistance, protect the imprinting and upgrade the additional value of printed matter. Have certain resistance to alkaline (NAOH), non-toxic, no smell, strong sense of transparency, no organic volatile emissions, without excitant odor, etc.
Product features:
O in-line printing machine with coating and off-line coating/glazing machine process
O high gloss degree
O good wearing resistance
O high chemical stability
O Eco-friendly, non-toxic
O Fast drying speed (can be adjusted as demans)
|
General physical property |
|
|
Appearance (visual) |
Milky white opacity liquid |
|
Solid content: % (150 ℃ ×30 minutes) |
42±2% |
|
PH value(PH meter) |
7.6 ~ 8.6 |
|
Viscosity: (T4#, 25 ℃ ) |
50±5s |
|
Glossiness: (60° angle) |
80±3° |
|
Wear resistance: (4-pound weight) |
400 times |
Applicaition:
Widely used for book coverage, publicity brochures, color boxes, medicine packages, labels, advertising display packing, etc. Various outer packages Which varnishing orders need high gloss degree.
Range of application ( applied coating machine ):
1.Sheet fed offset printing, roller coating/glazing/varnishing element.(Cavity scraper or double-roller).
2.Drying : IR or hot air.
3.In-line Offste printing with coating unit.
Using/operating recommendation :
1.Dilution rate: if in-line printing and coating, use it directly; if off-line coating process, please according to the actual situation dilute reasonable with water, insure the product quality.
2.Please fully stir and test the viscosity before using.
3.Coating weight: when in-line 3 ~ 5 g/m²,when off-line 4 ~ 6 g/m², in order to insure the gloss and wear resistance property. After finishing coating, the varnish must dry well and guarantee the performance of anti-blocking.
4.Please use the printing inks which fit for varnishing or coating. When choose inks should consider the resistance against alkali, alcohol and solvents, in order to exclude and color change.
5.when using the non-absorptive base printing material or using slow-drying printing inks, suggested setting aside corresponding drying time.
6.Recommended paper-pile temperature: not exceeding 35 ℃ .
7.Should have sufficient air flow between printed substrates, in order to insure rapid and complete drying, varnishing characters will be display fully after completely drying.
8.After finished the glazing, before the post processing, should test the printed substrates (paper-ink-varnish) whether they were complete drying and hardening. The printed substrates should be performed post processing when has a sufficiently & highly stability, thus reducing the influence of the mechanical tensile force and humidity on the post processing.
9.If can’t use up one time after opening, please note seal preservation. Please clean the production equipment timely after using, don’t idle for a long time not to clean.
Storage :
1.Keep from freezing, heating power and solar radiation.
2.Shelf time are 12 months from date of production.
3.Seal in the original container, suggested storage temperature environment is 5 ℃ -30 ℃ .
4.Keep from mixing with the other varnish or washing water.
5.If improper storage or the time is too long, maybe cause the viscosity raise and affect the using.