Chromium Zirconium Copper Alloys C18150

Cr: 0.50-1.50%
Zr: 0.05-0.25% Min.
Cu: Reminder
Note: Copper plus additions equal 99.5% minimum.

Specific Weight: 8.90g/cm ³

Specific Heat: 0.376J/g*k

Heat Conductivity: 320W/m*K

Electrical Resistivity:: 0.023 ohm*mm ² /m

Thermal Expansion Coefficient (20 °C to 200 °C m/m/°C): 17 x 10 ^-6

Electrical Conductivity: min 44 m/ohm*mm ² 80.00%IASC

Note:

1). the units are based upon Metric.

2). the typical physical properties apply to age hardened products.

Chromium Zirconium Copper C18150 is an excellent and unique copper alloy with high electrical conductivity, hardness, and ductility, moderate strength, and excellent resistance to softening at elevated temperatures. The addition of 0.1% zirconium (Zr) and 1.0% chromium (Cr) to copper results in a heat treatable alloy which may be solution treated and subsequently aged to produce these desirable properties. Rod is usually supplied from the mill in the fully aged and drawn condition so no further heat treatment is required by the fabricator. The softening temperature of properly heat treated C18150 rod exceeds 500°C as compared to unalloyed pure copper which softens at 200°C, and silver bearing coppers which soften at 350°C.
Furthermore, many evidences shows that C18150 can provide less sticking and resisting deformation longer than its C18200 counterpart in some specific situatons.

Packing Details : in plywoode cases or wooden cases

Beryllium Copper plate

Beryllium Copper Pipe

we can provide special specification forms according to customers' requests.
We are also a manufacturer,so we can provide the products in conformity with your requirements.
Our company has rich technical force and advanced production equipment and coordinated advanced test equipment and method.