- Product Details
- {{item.text}}
Quick Details
-
Application:
-
Building, Concrete
-
Design Style:
-
Chinese
-
Place of Origin:
-
Beijing, China
-
Brand Name:
-
LW
-
Model Number:
-
PVC WATERSTOP, LW-PVC waterstop
-
Shape:
-
WATERSTOP
-
Core Material:
-
PVC
-
Format:
-
PVC WATERSTOP
-
Tensile strength (Normal Temp.),Mpa,≥:
-
12
-
Elongation ratio at break,%, ≥:
-
250
-
tearing strength, Kn/m ≥:
-
40
-
℃ ≤ Bend at low Temp.:
-
-20
-
Product Name:
-
Water stop joint
-
Usage:
-
Engineering Construction Waterproofing
-
Other name:
-
PVC waterstop
Quick Details
-
Warranty:
-
More than 5 years
-
After-sale Service:
-
Online technical support
-
Project Solution Capability:
-
Others
-
Application:
-
Building, Concrete
-
Design Style:
-
Chinese
-
Place of Origin:
-
Beijing, China
-
Brand Name:
-
LW
-
Model Number:
-
PVC WATERSTOP, LW-PVC waterstop
-
Shape:
-
WATERSTOP
-
Core Material:
-
PVC
-
Format:
-
PVC WATERSTOP
-
Tensile strength (Normal Temp.),Mpa,≥:
-
12
-
Elongation ratio at break,%, ≥:
-
250
-
tearing strength, Kn/m ≥:
-
40
-
℃ ≤ Bend at low Temp.:
-
-20
-
Product Name:
-
Water stop joint
-
Usage:
-
Engineering Construction Waterproofing
-
Other name:
-
PVC waterstop
Waterstop heater blade waterstop accessories pvc water stopper jointing procedure
1.High performance, corrosion-resistance, aging resistance, high strength, high tear resistance
2.Good toughness, not easy to break, long service life
3.High expansion ratio and good water sealing performance
4.Strict workmanship, environmental protection and non-toxic
5.Factory source, good quality and low price
Don't hesitate, come to me and place an order!
LangWei VS other
A variety of specifications for your choice
1.Middle buried waterstop 2.External water stop 3. Steel plate waterstop
Tech. Data:
|
No. |
items |
index |
|
|
1 |
Tensile strength (Normal Temp.), Mpa , ≥ |
12 |
|
|
2 |
Elongation ratio at break, % , ≥ |
250 |
|
|
3 |
tearing strength, Kn/m ≥ |
40 |
|
|
4 |
℃ ≤ Bend at low Temp. |
-20 |
|
|
5 |
Hot air aging ( 80℃×168h ) |
% ≥conservation rate of tensile strength at break |
80 |
|
% ≥conservation rate of elongation ratio at break |
70 |
||
|
appearance of 100% elongation ratio |
No cracks |
||
|
6 |
( 10%Ca(OH ) 2 ×168h) Alkali-resistant |
% ≥conservation rate of tensile strength at break |
80 |
|
% ≥conservation rate of elongation ratio at break |
80 |
||