Quick Details
-
CaO Content (%):
-
1.-2.5%
-
CrO Content (%):
-
0.01%
-
SiC Content (%):
-
/
-
Place of Origin:
-
Henan, China, HeNan, China
-
Brand Name:
-
KEDA
-
Model Number:
-
MG-91/MG-92/MG-95A/MG-95B/MG-97A/MG-97B/MG-98
-
Cold Crushing Strength:
-
60MPa
-
Refractoriness Under Load @0.2MPa:
-
1250℃-1350℃
-
Bulk Density:
-
2.9~3.0g/cm3
-
Apparent Porosity:
-
17%~18%
Quick Details
-
SiO2 Content (%):
-
0.6-4.0%
-
Al2O3 Content (%):
-
0.1-0.8%
-
MgO Content (%):
-
92-97.5%
-
CaO Content (%):
-
1.-2.5%
-
CrO Content (%):
-
0.01%
-
SiC Content (%):
-
/
-
Place of Origin:
-
Henan, China, HeNan, China
-
Brand Name:
-
KEDA
-
Model Number:
-
MG-91/MG-92/MG-95A/MG-95B/MG-97A/MG-97B/MG-98
-
Cold Crushing Strength:
-
60MPa
-
Refractoriness Under Load @0.2MPa:
-
1250℃-1350℃
-
Bulk Density:
-
2.9~3.0g/cm3
-
Apparent Porosity:
-
17%~18%
Keda provides a full range of high-temperature mullite insulation bricks and magnesium iron spinel bricks, mainly used in non-ferrous smelting, transition zones before and after cement rotary kilns, high-temperature zones of lime kilns, glass thermal storage types, and furnace tops of reflection furnaces.
| Brand Properties | MH brick | |
| Application Limit Temp | 1790 | |
| Bulk Density (g/cm3) | 2.95 | |
| Cold Crushing Strength (MPa) | 45 | |
| Thermal Shock Resistance at 1,100°C Water cooling | 6 | |
| Refractoriness under Load (0.2MPa,T2°C) | 1680 | |
| ChemicalComposition (%) | MgO | 80 |
| Al203 | 4.0 | |
| Fe203 | 4.0-6.0 | |
| Main Applications |
- burning zone in rotary kiln -transition zone in rotary kiln |
|