- Product Details
- {{item.text}}
Quick Details
-
CaO Content (%):
-
0.123
-
CrO Content (%):
-
0.22
-
SiC Content (%):
-
>89%
-
Place of Origin:
-
Jiangsu, China
-
Model Number:
-
YXJT-111PT
-
Brand Name:
-
KamTai
-
SiC:
-
>89%
-
Density:
-
2.65g/cm3
-
Apparent porosity:
-
<28%
-
Breaking strength:
-
>15Mpa
-
Working temperature:
-
1400℃
-
Name:
-
Refractory sillicon carbide plate
-
Advantage:
-
High temperature resistance
-
Sample:
-
For free
-
Feature:
-
Good thermal shock resistane
-
Application:
-
Firing magnetic material
Quick Details
-
SiO2 Content (%):
-
<10%
-
Al2O3 Content (%):
-
0.2
-
MgO Content (%):
-
0.1
-
CaO Content (%):
-
0.123
-
CrO Content (%):
-
0.22
-
SiC Content (%):
-
>89%
-
Place of Origin:
-
Jiangsu, China
-
Model Number:
-
YXJT-111PT
-
Brand Name:
-
KamTai
-
SiC:
-
>89%
-
Density:
-
2.65g/cm3
-
Apparent porosity:
-
<28%
-
Breaking strength:
-
>15Mpa
-
Working temperature:
-
1400℃
-
Name:
-
Refractory sillicon carbide plate
-
Advantage:
-
High temperature resistance
-
Sample:
-
For free
-
Feature:
-
Good thermal shock resistane
-
Application:
-
Firing magnetic material
1.Description
This kiln shelf( we also call it sandwich plate ) is made of high purity mullite and corundum,collocation of silicon carbide composite three-layer heart shed board,which has high load softening point and high stability,low pollution.Applied to the manganese zinc ferrite and other forms of electronic ceramics firing process.
2.Features
1.High temperature tolerance
2.Corrosion resistance
3.Oxidation resistance.
4.Wear resistance
3.Technical data
|
Al2O3 |
>70%Outside |
|
SiO2 |
<28% |
|
Sic |
>85%Inside |
|
Apparent porosity |
<28% |
|
Density |
2.65g/cm3 |
|
Breaking strength |
>15Mpa |
|
Working temperature |
1300 ℃ |
4. Application (sintering magnetic material )
We can offer whole set of this application ,including sandwich plate , corundum-mullite setter plate and corundum kiln post.