- Product Details
- {{item.text}}
Quick Details
-
Application:
-
Hotel
-
Design Style:
-
Modern
-
Place of Origin:
-
Shandong, China
-
Brand Name:
-
Chensheng
-
Model Number:
-
XX-PVC
-
Product Name:
-
PVC Roofing PVC Waterproof Membrane for Construction
-
Main Raw Material:
-
polyvinyl chloride colophony
-
Thickness:
-
1.0/1.2/1.5/2.0mm
-
Width:
-
1.05/2.05m
-
Length:
-
20m/roll
-
Usage:
-
Waterproof Projects,the roof of building,underground building,etc
-
Color:
-
Customized Color
-
Surface material:
-
H/Polyester fabric
-
Certificate:
-
ISO9001, ISO14001, CE
-
Roll size:
-
41 square/roll
Quick Details
-
Warranty:
-
More than 5 years
-
After-sale Service:
-
Online technical support
-
Project Solution Capability:
-
graphic design
-
Application:
-
Hotel
-
Design Style:
-
Modern
-
Place of Origin:
-
Shandong, China
-
Brand Name:
-
Chensheng
-
Model Number:
-
XX-PVC
-
Product Name:
-
PVC Roofing PVC Waterproof Membrane for Construction
-
Main Raw Material:
-
polyvinyl chloride colophony
-
Thickness:
-
1.0/1.2/1.5/2.0mm
-
Width:
-
1.05/2.05m
-
Length:
-
20m/roll
-
Usage:
-
Waterproof Projects,the roof of building,underground building,etc
-
Color:
-
Customized Color
-
Surface material:
-
H/Polyester fabric
-
Certificate:
-
ISO9001, ISO14001, CE
-
Roll size:
-
41 square/roll
PVC Roll PVC Waterproof Membrane for Construction
Polyvinyl Chloride(PVC) waterproof membrane is a new polymer waterproof membrane. The raw material is polyvinyl chloride resin, mixed with plasticizer, filler, antioxygen, ultravoilet absorber and other auxiliaries.
|
N1 |
PVC membrane without compound layer for exposed |
|
N2 |
PVC membrane without compound layer for non exposed |
|
L1 |
PVC membrane with compound layer for exposed |
|
L2 |
PVC membrane with compound layer for non exposed |
|
W1 |
PVC reinforced membrane for exposed |
|
W2 |
PVC reinforced membrane for non exposed |
Technical data
|
No. |
Item |
L |
N |
W |
||||
|
I |
II |
I |
II |
I |
II |
|||
|
1 |
Tensile strength N/cm ≥ |
100 |
160 |
8 |
12 |
100 |
160 |
|
|
2 |
fracture elongation %≥ |
150 |
200 |
200 |
200 |
150 |
200 |
|
|
3 |
Dimension Changing at heating %≤ |
1.5 |
1 |
3 |
2 |
1.5 |
1 |
|
|
4 |
Foldability at low temperature °C |
-20 |
-25 |
-20 |
-25 |
-20 |
-25 |
|
|
5 |
Water tightness |
No leakage |
No leakage |
No Leakage |
||||
|
6 |
Joint shear resistance (N/mm)≥ |
3 |
3 |
6 |
||||
|
7 |
Thermal Ageing treatment |
Appearance |
no bubble |
no bubble |
no bubble |
|||
|
Tensile strength changing rate % |
±25 |
±20 |
±25 |
±20 |
±25 |
±20 |
||
|
Breaking elongation changing rate% |
||||||||
|
8 |
Chemical corrosion resistance |
foldability at low temperature °C |
-15 |
-20 |
-15 |
-20 |
-15 |
-20 |
|
Tensile strength changing rate % |
±25 |
±20 |
±25 |
±20 |
±25 |
±20 |
||
|
Breaking elongation changing rate% |
||||||||
|
9 |
Artificial climate accelerated aging |
foldability at low temperature °C |
-15 |
-20 |
-15 |
-20 |
-15 |
-25 |
|
Tensile strength changing rate % |
±25 |
±20 |
±25 |
±20 |
±25 |
±20 |
||
|
Breaking elongation changing rate% |
||||||||