Quick Details
-
Brand Name:
-
HaoRui
-
Dimension:
-
Customized
-
Color:
-
Ivory
-
Density:
-
6.02g/cm3
-
Bending Strength:
-
800MPa
-
Compressive Strength:
-
3000Mpa
-
Thermal Conductivity:
-
3W/mK
-
Max Working Temperature:
-
1000℃
-
Volume Resistance:
-
>1013Ωcm
-
Feature:
-
Good mechanical properties.
-
Certification:
-
ISO9001:2015
Quick Details
-
Material:
-
Zirconia Ceramic
-
Place of Origin:
-
Guangdong, China
-
Model Number:
-
ZrO2-06
-
Brand Name:
-
HaoRui
-
Dimension:
-
Customized
-
Color:
-
Ivory
-
Density:
-
6.02g/cm3
-
Bending Strength:
-
800MPa
-
Compressive Strength:
-
3000Mpa
-
Thermal Conductivity:
-
3W/mK
-
Max Working Temperature:
-
1000℃
-
Volume Resistance:
-
>1013Ωcm
-
Feature:
-
Good mechanical properties.
-
Certification:
-
ISO9001:2015
Product Paramenters
|
Property
|
Item
|
99%
Alumina
|
99.8%
Alumina
|
Zirconia Ceramics
|
Silicon Nitride
|
Silicon Carbide
|
Unit
|
|
Mechanical Characteristics |
Color |
light yellow
|
White |
Ivory |
Black
Grey |
Black |
|
|
|
Bulk Density
|
3.85
|
3.93
|
6.02
|
3.2
|
3.16
|
g/cm3
|
|
|
Water Absorption
|
0
|
0
|
0
|
0
|
0
|
%
|
|
|
Bending Strength
|
310
|
370
|
800
|
750
|
450
|
MPa
|
|
|
Compressive Trength
|
2,400
|
2500
|
3000
|
3800
|
3900
|
MPa
|
|
|
Elastic Modulus
|
340
|
390
|
200
|
290
|
420
|
GPa
|
|
|
Fracture Toughness
|
3~4
|
4
|
8
|
7
|
3.5
|
MPa m1/2
|
|
|
Weber Coefficient
|
12
|
12
|
15
|
15
|
-
|
m
|
|
|
Vickers Hardness
|
1,600
|
1850
|
1200
|
1700
|
2800
|
HV 0.5
|
|
Thermal Characterics |
Coefficient of Line Thermal
Expansion |
7~8 |
7~8 |
10 |
2 |
3.7 |
10-6 K-1 |
|
|
Thermal Conductivity
|
29
|
32
|
3
|
20
|
160
|
W/mK
|
|
|
Thermal Shock Resistance
(Put in Water) |
200 |
280 |
300 |
750 |
- |
ΔT °C |
|
|
Max Working Temperature
|
1,600 |
1700 |
1000 |
1300 |
1950 |
°C |
|
Electrical Characteristics |
Volume Resistance At 20°C
|
>1014 |
>1014 |
>1013 |
>1014 |
- |
Ωcm |
|
|
Dielectric Strength
|
15×106
|
15×106
|
11×106
|
10×106
|
-
|
V/m
|
|
|
Dielectric Constant
|
10
|
10
|
33
|
-
|
-
|
εr
|
|
|
One MHZ Dielectric Loss Angle
at 20°C |
0.0002 |
0.0001 |
0.0016 |
- |
- |
tanδ |
|
Chemical Characteristics |
Nitric Acid (60%) 90°C
|
0.1
|
0.05
|
≒0.00
|
1
|
≒0.00
|
24H WT Loss mg/cm2 |
|
|
Sulphuric Acid (95%) 95°C
|
0.34
|
0.22
|
0.04
|
≒0.00
|
≒0.00
|
|
|
|
Caustic Soda (30%) 80°C
|
0.95
|
0.04
|
0.08
|
0.2
|
≒0.00
|
|
With unique ceramic precision machining technology, formed material is cut and lapped after sintering to required shapes. These products are used for their unrivaled performance in OA sliding parts as general structural members, precision jigs and tools, in wear and chemical resistant sliding parts and also in electromagnetic fields and chemical solutions.
|
Process range
|
|
|
|
|
|
|||||
|
Inside Diameter
|
≥0.2mm
|
Length
|
≤750mm
|
Internal thread
|
≥2mm
|
|||||
|
Outside Diameter
|
≤400mm
|
Thickness
|
≤400mm
|
External thread
|
≤400mm
|
|||||
|
Machining accuracy
|
|
|
|
|
|
|||||
|
roundness
|
0.002mm
|
Parallelism
|
0.003mm
|
Verticality
|
0.005mm
|
|||||
|
concentricity
|
0.002mm
|
Flatnes
|
0.002mm
|
Straightness
|
0.005mm
|
|||||
|
clearance fit
|
0.003mm
|
tolerance of dimension
|
0.001mm
|
surface roughness
|
Ra0.1
|
|||||
Customizable Custom Industrial 3mol Ysz Zirconia Ceramic Machining Part Ceramic tube