Quick Details
-
CaO Content (%):
-
0.01%
-
CrO Content (%):
-
0.01%
-
SiC Content (%):
-
0.01%
-
Place of Origin:
-
Henan, China, Henan, China
-
Brand Name:
-
KEDA
-
Product name:
-
silica fire brick refractory materials for glass kiln
-
Application:
-
Furnace
-
Raw material:
-
quartzite
-
Size:
-
230*114*65mm
-
BULK DENSITY:
-
≤2.35g/cm³
-
Usage:
-
glass kiln
Quick Details
-
SiO2 Content (%):
-
94%
-
Al2O3 Content (%):
-
0.001%
-
MgO Content (%):
-
0.01%
-
CaO Content (%):
-
0.01%
-
CrO Content (%):
-
0.01%
-
SiC Content (%):
-
0.01%
-
Place of Origin:
-
Henan, China, Henan, China
-
Brand Name:
-
KEDA
-
Product name:
-
silica fire brick refractory materials for glass kiln
-
Application:
-
Furnace
-
Raw material:
-
quartzite
-
Size:
-
230*114*65mm
-
BULK DENSITY:
-
≤2.35g/cm³
-
Usage:
-
glass kiln
|
Brand
Properties |
GZ-96 | GZ-95 | GZ-94 | |
| Chemical Composition (%) | sio2 | ≥96 | ≥95 | ≥94 |
| Fe203 | ≤1.0 | ≤1.2 | ≤1.4 | |
| Apparent Porosity (%) | ≤22 | ≤22 | ≤22 | |
| True Density (g/cm3) | ≤2.34 | ≤2.35 | ≤2.35 | |
| Cold Crushing Strength (MPa) | ≥30 | ≥30 | ≥30 | |
| @0.2MPa Refractoriness Under Load (C | ≥1660 | ≥1650 | ≥1640 | |
| Main Applications |
-Hot-blast furnace -Coke oven -Glass kiln |
|||