- Product Details
- {{item.text}}
Quick Details
-
Product name:
-
Electronic Silicone Encapsulants
-
Application:
-
Electronic potting
-
Color:
-
A: Grey B: White
-
Mixing ratio:
-
1:1
-
Working time:
-
30-40 Mins
-
Curing time:
-
24 Hours
-
Hardness:
-
56 shore A
-
Viscosity:
-
3600 Cps
-
Thermal Conductivity:
-
0.525*10-3Cm/°C
-
Shelf life:
-
12months Under 25C
Quick Details
-
Place of Origin:
-
Guangdong, China
-
Brand Name:
-
MCsilicone
-
Model Number:
-
MC- RTV160
-
Product name:
-
Electronic Silicone Encapsulants
-
Application:
-
Electronic potting
-
Color:
-
A: Grey B: White
-
Mixing ratio:
-
1:1
-
Working time:
-
30-40 Mins
-
Curing time:
-
24 Hours
-
Hardness:
-
56 shore A
-
Viscosity:
-
3600 Cps
-
Thermal Conductivity:
-
0.525*10-3Cm/°C
-
Shelf life:
-
12months Under 25C
Product Description
Silicone Encapsulant 160 Silicone Elastomer is a two component, room temperature or heat curing encapsulant that is used for general potting applications of power supplies. It has good flowability, moderate thermal conductivity, and flame resistance.
Instructions
1. The curing time varies due to different temperature, the higher temperature, it cures faster. Users can adjust the ratio of
catalyst according to the temperature in order to get an ideal curing speed.
2. Certain materials can inhibit the cure of Silicone rubber. The most notable include: sulfur, polysulfide, sulfur-containing
material, Organ tin and organ metallic compound, etc.
3. Prevent from contact with tin, phosphorus, water, ammonium, chlorine, carboxylic acid, hydroxyl compound, etc. to avoid un-curing circumstance.
Silicone compound part A and Part B should be thoroughly mixed at a 1:1 ratio (weight) before using. Pour into the electronic components after vacuum de-airing. Silicone compound may be cured at room temperature or accelerated with heat.
Precautions
1. The curing time varies due to different temperature, the higher temperature, it cures faster. Users can adjust the ratio of
catalyst according to the temperature in order to get an ideal curing speed.
2. Certain materials can inhibit the cure of Silicone rubber. The most notable include: sulfur, polysulfide, sulfur-containing
material, Organ tin and organ metallic compound, etc.
3. Prevent from contact with tin, phosphorus, water, ammonium, chlorine, carboxylic acid, hydroxyl compound, etc. to avoid un-curing circumstance.
Specification
|
Item No.
|
MCSIL-E160A/B
|
|
|
Before curing
|
|
|
|
Appearance
|
A:Grey B: White
|
|
|
Viscosity (mPa.s 25°C)
|
3000~6000
|
|
|
Working life (min 25°C)
|
30
|
|
|
Curing time (hrs)
|
24
|
|
|
Heat-up at 100°C (min)
|
10
|
|
|
After curing
|
|
|
|
Hardness (shore A)
|
50~60
|
|
|
Dielectric breakdown voltage kv/mm 25°C
|
≥20
|
|
|
Volume resistivity ohm*cm
|
1*1015
|
|
|
Tensile Strength Mpa
|
≥0.6
|
|
|
Thermal conductivity cm/°C
|
0.525*10-3
|
|
|
Working temperature °C
|
-30~200
|
|
Packing & Delivery
Packs are available in 20kg and 200kg per drum.
1. Silicone rubber is shipped as kits that Part A and B liquid components in separate containers. It is available in packing in 5kg or 20kg,200kg per pail.
2. Silicone rubber must be tightly sealed in cool and dry place, prevented from sun and rain. Transport by non-dangerous goods.
2. Silicone rubber must be tightly sealed in cool and dry place, prevented from sun and rain. Transport by non-dangerous goods.
Hot Searches