TYPICAL PROPERTIES (1)
|
|
|
|
|
MECHANICAL
|
Value
|
Unit
|
Standard
|
|
Tensile Stress, yld, Type I, 50 mm/min
|
63
|
MPa
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
56
|
MPa
|
ASTM D 638
|
|
Tensile Stress, yld, Type I, 5 mm/min
|
59
|
MPa
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 5 mm/min
|
66
|
MPa
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
4.3
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
>100
|
%
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 5 mm/min
|
4.2
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 5 mm/min
|
>100
|
%
|
ASTM D 638
|
|
Tensile Modulus, 5 mm/min
|
2590
|
MPa
|
ASTM D 638
|
|
Tensile Stress, yield, 5 mm/min
|
62
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 5 mm/min
|
51
|
MPa
|
ISO 527
|
|
Tensile Stress, yield, 50 mm/min
|
60
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 50 mm/min
|
45
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 5 mm/min
|
4.3
|
%
|
ISO 527
|
|
Tensile Strain, break, 5 mm/min
|
>50
|
%
|
ISO 527
|
|
Tensile Strain, yield, 50 mm/min
|
4.4
|
%
|
ISO 527
|
|
Tensile Strain, break, 50 mm/min
|
>50
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min
|
2520
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min
|
93
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min
|
2510
|
MPa
|
ISO 178
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
Izod Impact, notched, 23°C
|
385
|
J/m
|
ASTM D 256
|
|
Izod Impact, notched, 0°C
|
290
|
J/m
|
ASTM D 256
|
|
Izod Impact, notched 80*10*4 +23°C
|
17
|
kJ/m²
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*4 0°C
|
12
|
kJ/m²
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*4 -30°C
|
9
|
kJ/m²
|
ISO 180/1A
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
15
|
kJ/m²
|
ISO 179/1eA
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
CTE, -30°C to 80°C, flow
|
6.9E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, -30°C to 80°C, xflow
|
7.1E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, 23°C to 80°C, xflow
|
7.5E-05
|
1/°C
|
ISO 11359-2
|
|
Ball Pressure Test, 75°C +/- 2°C
|
PASSES
|
-
|
IEC 60695-10-2
|
|
Vicat Softening Temp, Rate A/50
|
111
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/50
|
102
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120
|
104
|
°C
|
ISO 306
|
|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm
|
99
|
°C
|
ISO 75/Be
|
|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
|
88
|
°C
|
ISO 75/Ae
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
Mold Shrinkage on Tensile Bar, flow (2)
|
0.4 - 0.6
|
%
|
SABIC Method
|
|
Density
|
1.17
|
g/cm³
|
ISO 1183
|
|
Water Absorption, (23°C/sat)
|
0.6
|
%
|
ISO 62
|
|
Moisture Absorption (23°C / 50% RH)
|
0.2
|
%
|
ISO 62
|
|
Melt Volume Rate, MVR at 260°C/2.16 kg
|
13
|
cm³/10 min
|
ISO 1133
|
|
FLAME CHARACTERISTICS
|
Value
|
Unit
|
Standard
|
|
UL Compliant, 94V-0 Flame Class Rating (3)(4)
|
2
|
mm
|
UL 94 by GE
|
|
Glow Wire Flammability Index 960°C, passes at
|
1
|
mm
|
IEC 60695-2-12
|
|
Oxygen Index (LOI)
|
29
|
%
|
ISO 4589
|
|
UV-light, water exposure/immersion
|
F1
|
-
|
UL 746C
|
|