- Product Details
- {{item.text}}
Quick Details
-
Surface Finish:
-
2B
-
Invoicing:
-
by theoretical weight
-
Place of Origin:
-
China
-
Brand Name:
-
Gnee
-
Application:
-
Processing equipment, machinery parts, etc.
-
Width:
-
60-2000mm
-
Product Name:
-
304 Stainless Sheet 2mm 304 Stainless Steel Plate Suppliers
-
Related Grade:
-
304L, 304H
-
Cooperative Steel Mill:
-
TISCO BAOSTEEL POSCO JISCO LISCO
-
Size:
-
0.15-150mm*10-2000mm*L
-
Surface:
-
No.1 2B BA 8K Mirror Hairline satin Embossed brush No.4 HL
-
Supplied Forms:
-
Sheet, Strip, Bar, Plate, Pipe, Tube, Coil, Fittings
-
Equivalent Grade:
-
SUS304, 1.4301, S30400, 304S15, 304S16, 304S31 and EN58E.
-
Type:
-
Plate
Quick Details
-
Thickness:
-
0.1-6.0mm
-
Tolerance:
-
±0.1mm
-
Steel Grade:
-
301L, S30815, 301, 304N, 310S, S32305, 410, 204C3, 316Ti, 316L, 441, 316, L4, 420J1, 321, 410S, 410L, 436L, 443, LH, L1, S32304, 314, 347, 430, 309S, 304, 439, 204C2, 425M, 409L, 420J2, 436, 445, 304L, 405, 370, S32101, 904L, 444, 301LN, 305, 429, 304J1, 317L
-
Surface Finish:
-
2B
-
Invoicing:
-
by theoretical weight
-
Place of Origin:
-
China
-
Brand Name:
-
Gnee
-
Application:
-
Processing equipment, machinery parts, etc.
-
Width:
-
60-2000mm
-
Product Name:
-
304 Stainless Sheet 2mm 304 Stainless Steel Plate Suppliers
-
Related Grade:
-
304L, 304H
-
Cooperative Steel Mill:
-
TISCO BAOSTEEL POSCO JISCO LISCO
-
Size:
-
0.15-150mm*10-2000mm*L
-
Surface:
-
No.1 2B BA 8K Mirror Hairline satin Embossed brush No.4 HL
-
Supplied Forms:
-
Sheet, Strip, Bar, Plate, Pipe, Tube, Coil, Fittings
-
Equivalent Grade:
-
SUS304, 1.4301, S30400, 304S15, 304S16, 304S31 and EN58E.
-
Type:
-
Plate
304 Stainless Sheet 2mm 304 Stainless Steel Plate Suppliers
Stainless steel 304 also known as 1.4301 respectively. Type 304 is the most versatile and widely used stainless steel.
It is still sometimes referred to by its old name 18/8 which is derived from the nominal composition of type 304 being 18% chromium and 8% nickel.
Chemical Composition
|
Grade |
C |
Mn |
Si |
P |
S |
Cr |
Mo |
Ni |
N |
|
|
304 |
min.
|
-
|
-
|
-
|
-
|
-
|
18.0
|
- |
8.0
|
-
|
Mechanical Properties
|
Grade |
Tensile Strength (MPa) min |
Yield Strength 0.2% Proof (MPa) min |
Elongation (% in 50 mm) min |
Hardness |
|
|
Rockwell B (HR B) max |
Brinell (HB) max |
||||
|
304 |
515 |
205 |
40 |
92 |
201 |
Physical Properties
|
Density (kg/m3) |
Elastic Modulus (GPa) |
Mean Coefficient of Thermal Expansion (μm/m/°C) |
Thermal Conductivity (W/m.K) |
Specific Heat 0-100 °C (J/kg.K) |
Electrical Resistivity (nΩ.m) |
||||
|
0-100 °C |
0-315 °C |
0-538 °C |
at 100 °C |
at 500 °C |
|||||
|
304/L/H |
8000 |
193 |
17.2 |
17.8 |
18.4 |
16.2 |
21.5 |
500 |
720 |
Equivalent Grade
|
Grade |
UNS No |
Old British |
Euronorm |
Swedish SS |
Japanese JIS |
||
|
BS |
En |
No |
Name |
||||
|
304 |
S30400 |
304S31 |
58E |
1.4301 |
X5CrNi18-10 |
2332 |
SUS 304 |
Possible Alternative Grades
|
Grade |
Why it might be chosen instead of 304 |
|
301L |
A higher work hardening rate grade is required for certain roll formed or stretch formed components. |
|
302HQ |
Lower work hardening rate is needed for cold forging of screws, bolts and rivets. |
|
303 |
Higher machinability needed, and the lower corrosion resistance, formability and weldability are acceptable. |
|
316 |
Higher resistance to pitting and crevice corrosion is required, in chloride environments |
|
321 |
Better resistance to temperatures of around 600-900 °C is needed…321 has higher hot strength. |
|
3CR12 |
A lower cost is required, and the reduced corrosion resistance and resulting discolouration are acceptable. |
|
430 |
A lower cost is required, and the reduced corrosion resistance and fabrication characteristics are acceptable. |