- Product Details
- {{item.text}}
Quick Details
-
Place of Origin:
-
China, CN;GUA
-
Type:
-
100% Biodegradeble Material
-
Sample:
-
Available
-
Material:
-
Biodegradable Polylactic Acid
-
Color:
-
Natural or Customized
-
MOQ:
-
1 KG
-
Product Name:
-
PLA Plastic Granule
Quick Details
-
color:
-
Transparent
-
Shape:
-
Pellets, Granules, Granule
-
Brand Name:
-
CHOZEN TECH, Chozen Tech
-
Place of Origin:
-
China, CN;GUA
-
Type:
-
100% Biodegradeble Material
-
Sample:
-
Available
-
Material:
-
Biodegradable Polylactic Acid
-
Color:
-
Natural or Customized
-
MOQ:
-
1 KG
-
Product Name:
-
PLA Plastic Granule
Polylactic Acid (PLA) is a biodegradable thermoplastic derived from renewable resources like corn starch or sugar cane. It's recognized for its environmental friendliness, as it produces fewer greenhouse gas emissions during production compared to many plastics derived from fossil fuels.
PLA has found widespread application due to its biodegradable nature. In the packaging industry, it's used to create compostable containers and bags. In medical applications, it's used for sutures and implants that naturally break down in the body over time. Moreover, PLA is a popular material in 3D printing due to its low melting point and ease of use. However, it is not suitable for high-temperature or high-moisture applications. As sustainability becomes increasingly important, PLA's use continues to expand.
As a mature and long-standing supplier, we can provide you with PLA products from various kinds of famous brand manufacturers.
For example,
NatureWorks LLC, Total Corbion PLA, BASF and Chinese brand.
The MOQ is available from 1 bag(25kg/55lbs). Shipped by international express, you can receive the goods within a few days.
|
Technical Items |
Test Standard |
T ypical Value |
|
Physical Properties |
||
|
Specific Gravity (g/cc) |
D792 |
1.24 |
|
MFR, g/10 min (210°C, 2.16kg) |
D1238 |
6 |
|
Relative Viscosity (RV measured at 1.0 g/dL in chloroform at 30°C) |
D5225 |
4.0 |
|
Clarity |
|
Transparent |
|
Peak Melt Temperature (°C) |
D3418 |
145-160 |
|
Glass Transition Temperature (°C) |
D3418 |
55-60 |
|
Mechanical Properties |
||
|
Tensile Strength at Break, psi (MPa) |
D882 |
7,700 (53) |
|
Tensile Yield Strength, psi (MPa) |
D882 |
8,700 (60) |
|
Tensile Modulus, psi ( M Pa) |
D882 |
524,000 (3.6) |
|
Tensile Elongation, % |
D882 |
6.0 |
|
Notched Izod Impact, ft-lb/in (J/m) |
D256 |
0.3 (16) |
|
Flexural Strength, psi (MPa) |
D790 |
12,000 (83) |
|
Flexural Modulus, psi (MPa) |
D790 |
555,000 (3.8) |
|
Heat Distortion Temperature, °C 66 psi (0.45 MPa) |
E2092 |
55 |