- Product Details
- {{item.text}}
Quick Details
-
initial/Final setting time:
-
200/250mins
-
Whiteness:
-
≥90
-
Standard consistency:
-
28%
-
Loss -on-ignition(L.O.I.):
-
10.33%
-
Sulfur trioxide(SO3):
-
2.18%
-
Magnesia(MgO):
-
2.76%
-
Color:
-
White
Quick Details
-
Item name:
-
White portland cement price per ton
-
Compressive Strength(Mpa) @ 28 days:
-
50
-
Cement Fineness:
-
423 m2/kg
-
initial/Final setting time:
-
200/250mins
-
Whiteness:
-
≥90
-
Standard consistency:
-
28%
-
Loss -on-ignition(L.O.I.):
-
10.33%
-
Sulfur trioxide(SO3):
-
2.18%
-
Magnesia(MgO):
-
2.76%
-
Color:
-
White
White portland cement price per ton
White Cement is widely applied in White/colorful concrete, Colorful roof, GRC board, Tile adhesive, Terrazzo, Pavers, Culture stone, Wall putty etc building and custruction area, especially for building decoration.
|
Index Name |
Internal Control Index |
GB/T2015-2005 Standards |
||
|
Intensity |
3 days |
28 days |
3 days |
28 days |
|
Flexural strength, Mpa |
5.0 |
7.5 |
3.5 |
6.5 |
|
Compressive strength, Mpa |
28.0 |
46.0 |
17.0 |
42.5 |
|
Fineness 80um, % |
≤ 0.4% |
Maximum 10% |
||
|
Initial setting time |
180 minutes |
No earlier than 45 minutes |
||
|
Final setting time |
220 minutes |
No later than 10 hours |
||
|
Whiteness (Hengte Value) |
≥89.0 |
Minimum 87 |
||
|
Standard consistency |
27 |
/ |
||
| Sulfur trioxide(%) | 3.08 |
≤3.5 |
||
SPECIFICATIONS FOR ORIDINARY PORTLAND CEMENT AS PER EN 197-1:2011/CEM II 42.5
|
Items |
Units |
Specification |
Test Results |
Test Method |
|
SiO2 |
% |
≤ 26.00 |
21.98% |
EN 196-2 |
|
Al2O3 |
% |
≤ 6.50 |
2.85% |
|
|
Fe2O3 |
% |
≤ 4.50 |
≤0.28% |
|
|
CaO |
% |
≥ 54.00 |
65.69% |
|
|
MgO |
% |
≤ 5.00 |
1.76% |
|
|
SO3 |
% |
≤ 3.5 |
3.28% |
|
|
Loss on Ignition, (LOI) |
% |
≤ 5.00 |
3.46 |
|
|
Insoluble Residue |
% |
≤ 5.00 |
0.59% |
|
|
Physical and Mechanical Properties |
||||
|
Finess test |
|
|
|
EN 196-6 |
|
- Blaine |
cm2/g |
≥ 3200 |
4420 |
|
|
- Retained content on sieve 75mm |
% |
< 15.0 |
0.4 |
|
|
Time of setting - Initial set - Final set |
Minutes |
≥ 75 < 420 |
170 225 |
EN 196-3 |
|
Soundness (LeChatelier) |
mm |
< 10.0 |
0.0 |
EN 196-3 |
|
Compressive strength |
MPa |
|
|
EN 196-1 |
|
2 Days |
≥ 20.0 |
36.0 |
||
|
3 Days |
- |
40.0 |
||
|
7 Days |
- |
48.5 |
||
|
28 Days |
≥ 42.5 |
57.2 |
||