Polyamide 66 compound, 25% glass fibre reinforced, heat stabilized, flame retardant with halogens, PBB and PBDE free. Designed for Electrical applications requiring self-extinguishing properties combined with excellent ignition resistance, this grade meets the most stringent safety requirements for insulating materials.Â
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | 60x60x2; ISO 294-4 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | 60x60x2; ISO 294-4 |
| Melt Flow |
25 g/10 min
@Load 10.0 kg, Temperature 220 °C |
25 g/10 min
@Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 90.0 MPa | 13100 psi | ISO 2039-1 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | >= 15 % | >= 15 % | 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 2.4 % | 2.4 % | 50 mm/min; ISO 527-1, -2 |
| Tensile Modulus | 2.20 GPa | 319 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 62.0 MPa | 8990 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.10 GPa | 305 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) |
12.0 kJ/m²
@Temperature -30.0 °C |
5.71 ft-lb/in²
@Temperature -22.0 °F |
ISO 180-1A |
|
23.0 kJ/m²
@Temperature 23.0 °C |
10.9 ft-lb/in²
@Temperature 73.4 °F |
ISO 180-1A | |
| Charpy Impact Unnotched |
15.0 J/cm²
@Temperature -30.0 °C |
71.4 ft-lb/in²
@Temperature -22.0 °F |
ISO 179-1eU |
|
NB
@Temperature 23.0 °C |
NB
@Temperature 73.4 °F |
ISO 179-1eU | |
| Charpy Impact, Notched |
1.40 J/cm²
@Temperature -30.0 °C |
6.66 ft-lb/in²
@Temperature -22.0 °F |
ISO 179-1eA |
|
2.40 J/cm²
@Temperature 23.0 °C |
11.4 ft-lb/in²
@Temperature 73.4 °F |
ISO 179-1eA | |