Acrylic sheet Color:
-
Clear
-
Material:
-
Acrylic-100% Lucite PMMA Imported
-
Acrylic panel Application:
-
Acrylic Swimming Pool, Acrylic Pool Window
-
Thickness range:
-
30mm-950mm
-
Acrylic Free samples:
-
Yes, express cost on customer
-
Acrylic sheet style:
-
cast acrylic panel
-
MOQ:
-
1pcs
-
Technology:
-
Dry thermostatic polymerization
Quick Details
-
Place of Origin:
-
Shanghai, China, Shanghai,China
-
Brand Name:
-
AUPOOL
-
Model Number:
-
AUPOOL
-
Acrylic sheet Color:
-
Clear
-
Material:
-
Acrylic-100% Lucite PMMA Imported
-
Acrylic panel Application:
-
Acrylic Swimming Pool, Acrylic Pool Window
-
Thickness range:
-
30mm-950mm
-
Acrylic Free samples:
-
Yes, express cost on customer
-
Acrylic sheet style:
-
cast acrylic panel
-
MOQ:
-
1pcs
-
Technology:
-
Dry thermostatic polymerization
Products Description
Acrylic Transparent Infinity Swimming Pool at Xiyunxuan Hotel Ipoh, Malaysia
Material Specification
|
NO.
|
Physical Property
|
ISO
|
Unit
|
Result
|
||||
|
1.
|
Specific gravity / density
|
D792
|
Kg/m
|
1175
|
||||
|
Optical
|
|
|
|
|
||||
|
2.
|
Luminous Transmittance
|
GB/T2410-2008
|
%
|
92.6
|
||||
|
3.
|
Haze
|
GB/T2410-2008
|
%
|
1.8
|
||||
|
Mechanical
|
|
|
|
|
||||
|
4.
|
Tensile Strength
|
527-2:2012
|
|
|
||||
|
|
a) Maximum tensile strength
|
|
MPa
|
80.7
|
||||
|
|
b) Elongation at break
|
|
%
|
4
|
||||
|
|
c)Tensile modulus
|
|
MPa
|
3010
|
||||
|
5.
|
Flexural Strength
|
178:2010
|
|
|
||||
|
|
a) Maximum flexural strength
|
|
MPa
|
87.7
|
||||
|
|
b) Maximum flexural strength
|
|
MPa
|
2900
|
||||
|
6.
|
Comintsane Yield Stress
|
604:2002
|
MPa
|
No Yield Point
|
||||
|
7.
|
Izod Notched Immpact Stress
|
D256-10 (Method c)
|
J/m
|
8
|
||||
|
8.
|
Shear Strength
|
D732-10
|
MPa
|
62.5
|
||||
|
9.
|
Rockwell Hardness
|
2039-2:1987
|
HRL
|
105
|
||||
|
Thermal
|
|
|
|
|
||||
|
10.
|
Flammability
|
UL94-2013 (7)
|
mm/min
|
24.1
|
||||
|
11.
|
Heat Deflection Temperature
|
75-2:2013(Method B)
|
°C
|
106.2
|
||||
|
12.
|
Glass Transition Temperature
|
11357-2:1999
|
|
|
||||
|
|
a)Teig
|
|
°C
|
105.6
|
||||
|
|
b)Tmg
|
|
°C
|
114.0
|
||||
|
|
c)Tefg
|
|
°C
|
122.3
|
||||
|
13.
|
Coefficient of Linear Thermal Expansion
|
11359-2:1999
|
°C
|
-40 to 110
|
||||
|
|
a)Parallel to flow
|
|
um/m-°C
|
78.60
|
||||
|
|
b)Perpendicular to flow
|
|
um/m-°C
|
80.56
|
||||
|
Others
|
|
|
|
|
||||
|
14.
|
Water Absorption
|
62:2008
|
%
|
0.12
|
||||
|
15.
|
Odor
|
|
|
None
|
||||
|
16.
|
Taste
|
|
|
None
|
||||