- Product Details
- {{item.text}}
Quick Details
-
Ultimate Strength (≥ MPa):
-
0.04
-
Density (kg/m³ ):
-
128
-
Length:
-
3600/7200mm
-
Working Temperature:
-
1000℃-1600℃
-
Fiber Diameter:
-
2.8mm
-
Shrinkage (1800 ℉, 3h):
-
3%
-
Model Number:
-
hx-c1
-
Brand Name:
-
huaxing
-
Place of Origin:
-
Beijing, China
-
Color:
-
White
Quick Details
-
Thickness:
-
6/12.5/20/25/50mm
-
Width:
-
610/1220mm
-
Chemical Composition:
-
Al2O3+SiO2+ ZrO2(Cr2O3)
-
Ultimate Strength (≥ MPa):
-
0.04
-
Density (kg/m³ ):
-
128
-
Length:
-
3600/7200mm
-
Working Temperature:
-
1000℃-1600℃
-
Fiber Diameter:
-
2.8mm
-
Shrinkage (1800 ℉, 3h):
-
3%
-
Model Number:
-
hx-c1
-
Brand Name:
-
huaxing
-
Place of Origin:
-
Beijing, China
-
Color:
-
White
Foam roof price heat insulation kiln materials muffle furnace poly crystalline alumina silica refractory ceramic fiber blankets
|
Thickness
|
10-50mm
|
|
Width
|
610
|
|
Chemical Composition
|
AL2O3, SiO2
|
|
Ultimate Strength (≥ MPa)
|
≥0.05
|
|
Density (kg/m³ )
|
128
|
|
Place of Origin
|
Beijing, China
|
|
Grade
|
HP (High Pure)
|
|
Application
|
Refractory
|
|
Length
|
3000/6000
|
|
Working Temperature
|
1050C
|
|
Fiber Diameter
|
3-5um
|
|
Shrinkage (1800 ℉, 3h)
|
(1800 ℉, 3h): -3(24h)
|
|
Thermal Conductivity
|
0.12-0.20w/m.k(600-800C)
|
|
Model Number
|
HX-C1
|
|
Color
|
White
|
|
Package
|
PE and PP bag
|
|
Application of ceramic fiber blanket
|
Industrial furnace, electricity boilers, gas turbine and nuclear power
|
|
Working Temperature
|
1100C/1260C/1360C/1430C (2012F/2300F/2480F/2600F)
|
|
Raw material
|
Ceramic Fibre
|
|
Package of ceramic fiber blanket
|
Woven bag or carton
|
|
Supply Ability
|
100000 Ton/Tons per Month
|
|
Item
|
|
Standard
|
High Pure
|
High Aluminum
|
Zirconium
|
|
|
Classification Temp(℃）
|
|
1260
|
1260
|
1360
|
1430
|
|
|
Service Temp(℃）
|
|
≤1050
|
≤1100
|
≤1200
|
≤1350
|
|
|
Color
|
|
White
|
White
|
White
|
White
|
|
|
Density(kg/m3)
|
|
96-128
|
96-128
|
96-128
|
96-128
|
|
|
Permanent linear shrinkage (%)
|
|
1000°C×24h≤3
|
1000°C×24h≤3
|
1200°C×24h≤3
|
1350°C×24h≤3
|
|
|
Thermal conductivity (average temperature(70±52) (w/m.k) ( 128kg/m3)
|
|
0.09(400°C)0.16(800°C)
|
0.09(400°C)0.16(800°C)
|
0.12(600°C)0.20(1000°C)
|
0.16(800°C)0.20(1000°C)
|
|
|
Tensile strength (MPa) ( 128kg/m3)
|
|
0.08-0.12
|
0.08-0.12
|
0.08-0.12
|
0.08-0.12
|
|
|
Chemical Composition（%） |
AL2O3
|
45-46
|
47-49
|
52-55
|
39-40
|
|
|
|
AL2O3+SiO2
|
97
|
99
|
99
|
-
|
|
|
|
AL2O3+SiO2+ZrO2
|
-
|
-
|
-
|
99
|
|
|
|
ZrO2
|
-
|
-
|
-
|
15-17
|
|
|
|
Fe2O3
|
≤1.0
|
≤0.2
|
≤0.2
|
≤0.2
|
|
|
|
Na2O+K2O
|
≤0.5
|
≤0.2
|
≤0.2
|
≤0.2
|
|