- Product Details
- {{item.text}}
Quick Details
-
Brand Name:
-
Ultramid
Quick Details
-
color:
-
black
-
Shape:
-
particle
-
Place of Origin:
-
Germany
-
Brand Name:
-
Ultramid
Glass fibre reinforced injection moulding grade for machinery components and housings of high stiffness and dimensional stability such as coil formers and bearing cages. Also used for electrically insulating parts.
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | 60x60x2; ISO 294-4 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | 60x60x2; ISO 294-4 |
| Melt Flow |
25 g/10 min
@Load 10.0 kg, Temperature 220 °C |
25 g/10 min
@Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 90.0 MPa | 13100 psi | ISO 2039-1 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | >= 15 % | >= 15 % | 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 2.4 % | 2.4 % | 50 mm/min; ISO 527-1, -2 |
| Tensile Modulus | 2.20 GPa | 319 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 62.0 MPa | 8990 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.10 GPa | 305 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) |
12.0 kJ/m²
@Temperature -30.0 °C |
5.71 ft-lb/in²
@Temperature -22.0 °F |
ISO 180-1A |
|
23.0 kJ/m²
@Temperature 23.0 °C |
10.9 ft-lb/in²
@Temperature 73.4 °F |
ISO 180-1A | |
| Charpy Impact Unnotched |
15.0 J/cm²
@Temperature -30.0 °C |
71.4 ft-lb/in²
@Temperature -22.0 °F |
ISO 179-1eU |
|
NB
@Temperature 23.0 °C |
NB
@Temperature 73.4 °F |
ISO 179-1eU | |
| Charpy Impact, Notched |
1.40 J/cm²
@Temperature -30.0 °C |
6.66 ft-lb/in²
@Temperature -22.0 °F |
ISO 179-1eA |
|
2.40 J/cm²
@Temperature 23.0 °C |
11.4 ft-lb/in²
@Temperature 73.4 °F |
ISO 179-1eA | |