Quick Details
-
Tensile Strength:
-
34.5Mpa
-
Standard Color:
-
Black,clear
-
Approval:
-
UL,VW-1
-
Meet:
-
ROHS,SAE-AMS-DTL-23053/18
-
Operating temperature:
-
-55to+175
-
Minimum shrink temperature:
-
175
-
Dielectric strength:
-
30kv/mm
-
Elongation at break:
-
150%
-
Elongation at break after aging:
-
100%
-
Brand:
-
Dicore
Quick Details
-
Place of Origin:
-
Guangdong, China
-
Brand Name:
-
Dicore
-
Model Number:
-
HHST-175
-
Tensile Strength:
-
34.5Mpa
-
Standard Color:
-
Black,clear
-
Approval:
-
UL,VW-1
-
Meet:
-
ROHS,SAE-AMS-DTL-23053/18
-
Operating temperature:
-
-55to+175
-
Minimum shrink temperature:
-
175
-
Dielectric strength:
-
30kv/mm
-
Elongation at break:
-
150%
-
Elongation at break after aging:
-
100%
-
Brand:
-
Dicore
175℃ Heat Shrink PVDF Tubing (KYNAR) HHST-175 is semi-rigid, excellent flame retardant heat-shrinkable Polyvinylidene fluoride (PVDF) tube for applications requiring high temperature performance, outstanding abrasion and cut through resistance or superior chemical and solvent resistant properties. It reliably protects wires, solder joints, terminals and connections and components from most industrial fuels, solvents and chemicals.
Features
>Approvals: UL, VW -1
>Meet: RoHS, SAE-AMS-DTL-23053/18
>Operating temperature: -55℃ to +175℃
>Minimum shrink temperature: 175℃
>Standard color: Clear
Technical Data
| Property | Test Method | Typical Data |
| Operating temperature |
IEC 216 |
-55℃ to +175℃ |
| Tensile strength |
ASTM D 2671 |
34.5MPa |
| Elongation at break |
ASTM D 2671 |
150% |
| Elongation at break after aging |
250℃/168hrs. |
100% |
| Heat shock |
300℃/1hr. |
No cracking |
| Cold bend |
-55℃/1hr. |
No cracking |
| Flammability |
VW -1 |
Pass |
| Volume resistance |
IEC 93 |
1013Ω.cm |
| Dielectric strength |
ASTM D 2671 |
30kV/mm |
Specifiction
| Normal size | As supplied(mm) | After recovered (mm) | Tube shape | Standard length (m/roll) | ||
| (inch) | (mm) | Inside diameter(Min.) | Inside diameter (Max.) | Wall thickness(Nom.) | ||
|
3/ 64 |
1.2 |
1.2 |
0.6 |
0.25±0.05 |
O |
200 |