- Product Details
- {{item.text}}
Quick Details
-
Brand Name:
-
BASE, Keyuan
-
Material:
-
Polyamide 6/66 Nylon6/66 Pa6/66
-
Color:
-
Black
-
Type:
-
100% Virgin Material
-
Product name:
-
PA6 Plastic Granules
-
Item:
-
Nylon Raw Material
Quick Details
-
color:
-
white
-
Shape:
-
particle, Pelltes
-
Place of Origin:
-
Hebei, China
-
Brand Name:
-
BASE, Keyuan
-
Material:
-
Polyamide 6/66 Nylon6/66 Pa6/66
-
Color:
-
Black
-
Type:
-
100% Virgin Material
-
Product name:
-
PA6 Plastic Granules
-
Item:
-
Nylon Raw Material
Product Description
PA66 (polyamide 66 or nylon 66), compared with PA6, PA66 is more widely used in the automotive industry, instrument housings and other products that require impact resistance and high strength requirements.
Widely used in the manufacture of parts of machinery, automobiles, chemical and electrical devices, such as gears, rollers, pulleys, roller shafts, impellers in pump bodies, fan blades, high-pressure seals, valve seats, gaskets, bushings, various handles , support frame, inner layer of wire package, etc.
Specification
|
Property
|
Test Method
|
Typical Value
|
Unit
|
|
Melt Flow Rate
|
ISO 1133 @ 190°C/2.16 kg
|
1.6
|
g/10 min
|
|
Melt Flow Rate
|
ISO 1133 @ 210°C/2.16 kg
|
3.7
|
g/10 min
|
|
Density
|
ISO 1183
|
1.19
|
g/cm3
|
|
Water vapor transmission rate
|
ASTM E96 @ 40°C 90RH
|
1.3
|
|
|
Oxygen transmission rate
|
@ 20°C 0RH
|
0.0059
|
|
|
Oxygen transmission rate
|
@ 20°C 65RH
|
0.0079
|
|
|
Oxygen transmission rate
|
@ 20°C 85RH
|
0.03
|
|
|
Tensile Strength at Break
|
ISO 527 @ 23°C
|
34
|
MPa
|
|
Tensile modulus
|
ISO 527 @ 23°C
|
2700
|
MPa
|
|
Elongation at Break
|
ISO 527 @ 23°C
|
15
|
%
|
|
Flexural modulus
|
ISO 178 @ 23°C
|
4800
|
MPa
|
|
Simply Supported Beam Unnotched Impact
|
ISO 179
|
2
|
Kj/m2
|
|
Hardness
|
ISO 2023
|
90
|
|
|
Crystallization temperature
|
ISO 11357
|
158
|
|
|
Glass transition temperature
|
ISO 11357
|
57
|
℃
|
|
Melting temperature
|
ISO 11357
|
183
|
℃
|