hexagonal bar carbon steel C35

steel hexagonal bar carbon steel

APPLICATIONS:

Plain carbon steel for mechanical engineering and automotive components.

It is usually supplied untreated but can be supplied to order in the normalized or finally heat treated (quenched and tempered to "Q" or "R" properties), which is adequate for a wide range of applications.

It is a very popular grade of through-hardening medium carbon steel, which is readily machinable in any condition. It is suitable for the manufacture of parts such as general-purpose axles and shafts, gears, bolts and studs. It can be further surface-hardened typically to 50-55 HRC by induction processes, producing components with enhanced wear resistance.

In its heat treated forms possesses good homogenous metallurgical structures, giving consistent machining properties.

RELATED SPECIFICATIONS:

European:     C40, C45, Ck40,Ck45, Cm40, Cm45,

Germany      DIN 1.1191  DIN1.1201

Great Britain:  BS970: 1955 EN8,

BS970/PD970: 1970 onwards 080M40, 080M46, 060A47

France:       AFNOR XC 42 TS , AFNOR XC 45 , AFNOR XC 48 , AFNOR XC42

Sweden:       SS 1672

Werkstoff  No.: 1.0511, 1.1186, 1.1189.

USA:         ASTM A29 , ASTM A510 , ASTM A519 ,

ASTM A576 , ASTM A682 ,

FED QQ-S-635 (C1045) , FED QQ-S-700 (1045) ,

SAE J403 , SAE J412 , SAE J414 , UNS G10450

SAE:         1045, 1049, 1039, 1040, 1042, 1043, 1045.

Japan:        JIS S 45C , JIS S 48 C

Chemical Composition(%):

Carbon        0.43-0.50

Silicon        0.17-0.37

Manganese    0.60-0.90

Phosphorus    0.04 max

Sulphur       0.04 max

Chrome       0.30 min

Process:  EAF/LD+LF+VOD+hot Rolled+Cold Drawn+Heat Treatment(optional)

Hot forming and heat treatment:

hot rolling:1100 - 850°C

Normalising:840 - 880°C/air

Soft annealing:680 - 710°C/furnace

Hardening:820 - 860°C/water, oil

Tempering:550 - 660°C

Treated for cold shearability +S:max. 255 HB

Soft annealed +A:max. 207 HB

SIZE RANGE:

Round:

Hot Rolled:  Dia less than 90mm

Length:2000-13000mm or as required

SURFACE FINISHES:

Black, Peeled K12, Cold Drawn, Turned & Polished H10, H11, Precision Ground H9, H8

4.Forged ratio: no less than 3:1

Test: Ultrasonic test according to SEP 1921-84

Certificate of Quality: issued in English, in addition the normal terms, production process, the mechanical property yield strength, tensile strength, elongation and hardness, forged ratio, UT test result, Grain size, heat treatment methods and the sample of is shown on the Certificate of Quality.

Packing: Plastic reel shaft, and bound, iron wire frame, the paper barrel etc

Delivery: products in stock can be prepared within 5 days after you make your order. Products as your order can be finished within 15 days less than 500 tons. If you have specific requirements can be finished within 7 days less than 500 tons.

Marking: Heat No. will be cold stamped and Steel grade, diameter mm, length mm, and  the manufacturer LOGO and weight kg is painted