Quick Details
-
Place of Origin:
-
China
-
Product name:
-
Polylactic Acid PLA Pellets Resin
-
Density:
-
1.20-1.30 Kg/L
-
Melting Point:
-
155-185
-
Package:
-
25KG
-
Certificate:
-
COA TDS MSDS
-
Grade:
-
Extrusion Grade
Quick Details
-
color:
-
white
-
Shape:
-
resin
-
Brand Name:
-
Simel
-
Place of Origin:
-
China
-
Product name:
-
Polylactic Acid PLA Pellets Resin
-
Density:
-
1.20-1.30 Kg/L
-
Melting Point:
-
155-185
-
Package:
-
25KG
-
Certificate:
-
COA TDS MSDS
-
Grade:
-
Extrusion Grade
Product Images
Products Description
Product Superiority
PLA polylactic acid resin, biological resin, degradable plastics.
Polylactic acid (PLA) is a novel biodegradable material made from starch derived from renewable plant resources such as maize. Lactic acid is produced from starch by fermentation and then transformed into polylactic acid by chemical synthesis. It has good biodegradability and can be completely degraded by microorganisms in nature after use, and eventually generate carbon dioxide and water. It does not pollute the environment, which is very beneficial to the protection of the environment. It is environmentally friendly material.
PLA polylactic acid resin, biological resin, degradable plastics.
Polylactic acid (PLA) is a novel biodegradable material made from starch derived from renewable plant resources such as maize. Lactic acid is produced from starch by fermentation and then transformed into polylactic acid by chemical synthesis. It has good biodegradability and can be completely degraded by microorganisms in nature after use, and eventually generate carbon dioxide and water. It does not pollute the environment, which is very beneficial to the protection of the environment. It is environmentally friendly material.
|
ITEM
|
UNIT
|
REFERENCE INDEX
|
|
Appearance
|
-
|
White or yellow cylindrical granules
|
|
Particle Diameter
|
mm
|
2~4
|
|
Density
|
g/cm3
|
1.25±0.05
|
|
Monomer
|
%
|
≤1
|
|
Melt Index(190ºC 2.16kg)
|
g/10min
|
1~30
|
|
Glass Transition Temperature
|
ºC
|
58~60
|
|
Melting Point
|
ºC
|
~160
|
|
Tensile Strength at Break
|
MPa
|
~50
|
|
Tensile Modulus
|
GPa
|
3.5~6.0
|
|
Impact Strength
|
J/m
|
10~13
|
|
Properties
|
Unit
|
Test Standard
|
Data
|
|
Density
|
g/cm3
|
ASTM D-792
|
1.22-1.23
|
|
Melt Index (210ºC,2.16kg)
|
g/10min
|
ASTM D-1238
|
4.12
|
|
Melt Temperature
|
ºC
|
DSC
|
170-190
|
|
Vicat Point A/120
|
ºC
|
ASTM D-648
|
55
|
|
Tensile Strength
|
MPa
|
ASTM D-638
|
61
|
|
Flexural Strength
|
MPa
|
ASTM D-790
|
73
|
|
Elongation Break
|
%
|
ASTM D-638
|
22
|
|
Water Absorption
|
%
|
ASTM D-570
|
<0.6
|
|
Impact Strength
|
KJ/m2
|
ASTM D-256
|
8.8
|
|
Printing Temperature
|
ºC
|
DSC
|
200-220
|
PLA is suitable for blow molding, thermoplastic and other processing methods, convenient processing, widely used. It can be used for processing all kinds of plastic products, packaged food, snack boxes, non-woven fabrics, industrial and civil fabrics. And then processed into agricultural fabric, health fabric, cloth, sanitary products, outdoor uv fabric, tent cloth, floor mat surface and so on, promising market prospects.