- Product Details
- {{item.text}}
Quick Details
-
Standard size:
-
1200X2400MM,1220X2440MM
-
Thickness range:
-
3-25mm
-
Edge:
-
tapered, bevelled, grooved
-
Surface:
-
standard or slurry treatment
-
Backside:
-
standard or sanding
-
Raw material:
-
MgO,MgCl2,wood dust,fiber glass mesh, non-asbeatos
-
Color:
-
Red,Green,Grey,White etc.
-
Certificates:
-
CE,ASTM ,SGS,ISO9001:2000 QC system
Quick Details
-
Place of Origin:
-
Jiangsu, China
-
Name:
-
Magnesium Oxide Perlite Fire Door Core Board
-
Density:
-
1.0-1.3
-
Standard size:
-
1200X2400MM,1220X2440MM
-
Thickness range:
-
3-25mm
-
Edge:
-
tapered, bevelled, grooved
-
Surface:
-
standard or slurry treatment
-
Backside:
-
standard or sanding
-
Raw material:
-
MgO,MgCl2,wood dust,fiber glass mesh, non-asbeatos
-
Color:
-
Red,Green,Grey,White etc.
-
Certificates:
-
CE,ASTM ,SGS,ISO9001:2000 QC system
Magnesium Oxide Perlite Fire Door Core Board
Raw Material
Magnesium Oxide Perlite Fire Door Core Board is made of high purity magnesium oxide, MGO sulfate (Mgoso4)
replace of magnesium chloride(Mgcl2), high strength fiber glass mesh, perlite, non-woven fabrics.
Key advantages
- Fireproof Waterproof
- No asbestos sweating
- Suitable for light steel frame
- Insulate against heat and Keep warm
Specifications
|
Magnesium Oxide Perlite Fire Door Core Board is a newly developed type of incombustible inorganic board on the basis of the traditional magnesium oxide board. It is also called mgo board or Mgo sulfate board. |
||||
| Item | Thickness | Size | Backside | Color |
| External wall | 10-12mm | 1220*2400/2700/3000mm | Textile/sanded |
white grey green yellow blue black |
| Flooring board | 15-16-18-20-22mm | 600*1200/2400/2700/3000mm | Textile/sanded | |
| Ceiling board | 3-4.5-6mm | 600/1200mm*600mm/1200mm | Textile/sanded | |
| Interior board | 6-8-9-10mm | 1220*2440/2700/3000mm | Textile/sanded | |
| Edges type |
|
|||
| Magnesium Oxide Perlite Fire Door Core Board customized size and types are available. | ||||
Magnesium Oxide Perlite Fire Door Core Board product show
fireproof board certification
1.Bending strength
|
Test item |
Test Method |
Test Result |
|
|
Bending strength |
AS/NZS 2908.2:2000 Section 8.1.2.1 |
Direction |
Modulus of rupture |
|
Machine direction |
13.8MPa |
||
|
Across machine direction |
12.6MPa |
||
|
Average |
13.2MPa |
||
|
Remark |
Specimen Dimensions:250mm*250mm*10mm,10pcs |
||
2.Water permeability
|
Test item |
Test Method |
Test Result |
|
|
Water permeability |
AS/NZS 2908.2:2000 Section 8.2.2 |
Specimen |
Test Result |
|
1 |
No formation of drops of water on underside of the sheet |
||
|
2 |
No formation of drops of water on underside of the sheet |
||
|
3 |
No formation of drops of water on underside of the sheet |
||
|
Remark |
Specimen Dimensions:600mm*600mm*10mm,3pc |
||
3. Mositure movement
|
Test item |
Test Method |
Test Result |
|
|
Mositure movement |
ASTM C1185-08(R2016)Section8 |
Specimen |
Linear change(%) |
|
Machine direction |
0.18 |
||
|
Across machine direction |
0.12 |
||
|
Average |
0.15 |
||
|
Remark |
Specimen Dimensions:76mm*05mm*10mm,1pcs per direction |
||
4.Falling Ball Impact
|
Test item |
Test Method |
Test Result/Observation |
|
Falling Ball Impact |
ASTM D1037-12 Section 21 |
Bottom surface crack at 900mmheight. Top surface crack at 950mm height |
|
Remark |
Impactor :steel ball Impactor mass: 535 g Impactor diameter: 51 mm |
|
OCM®products fireproof board all certificated according to ASTM and AU/NZS standards. More information please contact us.