- Product Details
- {{item.text}}
Quick Details
-
Brand Name:
-
NK
-
Model Number:
-
NKDC
-
Power Source:
-
none
-
Material:
-
Flora alumino silicate glass powder, Poly acrylic Acid
-
Quality Certification:
-
none
-
Product name:
-
Glass Ionomer Cement
-
Usage:
-
Luting,. filling
-
shade:
-
three colors, powder have color #1;#2;#3
-
compression strength:
-
100MPA
-
packing:
-
20g*3powder+16ml*3liquid/box, 50box/carton
-
GW:
-
10KG/CARTON, 50BOXES/CARTON
Quick Details
-
Warranty:
-
3 years
-
After-sale Service:
-
Return and Replacement
-
Place of Origin:
-
Shanghai, China
-
Brand Name:
-
NK
-
Model Number:
-
NKDC
-
Power Source:
-
none
-
Material:
-
Flora alumino silicate glass powder, Poly acrylic Acid
-
Quality Certification:
-
none
-
Product name:
-
Glass Ionomer Cement
-
Usage:
-
Luting,. filling
-
shade:
-
three colors, powder have color #1;#2;#3
-
compression strength:
-
100MPA
-
packing:
-
20g*3powder+16ml*3liquid/box, 50box/carton
-
GW:
-
10KG/CARTON, 50BOXES/CARTON
Glass ionomer cement
| material | Fluoroaluminosilicate glass powder and polyacrylate solution |
| application | restorative filling of class 111, V cavities, wedge-shaped defect, liner & base |
| shade | three colors |
| package | 3bottles powder*20g+3bottle liquid*16ml |
| quantity | high quality material |
| high compression strength, low polymerization heat | |
| certificate | ISO13485; CE |
| warranty | three years |
Product feature:
1. Recommended powder to liquid ratio is in an environment temperature of 23℃±1℃ and 50±10% relative humidity blending . As the lining, the powder liquid (mass) ratio is 2.3:1; For repair ing , the ratio of powder to liquid (mass) was 2.7:1;
2. While mixing, the powder is divided into two parts, half of the powder into the liquid agent to fully reconcile for 10 seconds, into the other half of the powder, fully reconcile, total the time should be less than 30 seconds; Working time is 1 ‘ 45 “ ;
3. The net curing time is 1.5 - 6min ;
4. The compressive strength of cement should be ≥100MPa ;
5. The acid corrosion of cement should be ≤0.17mm;
6. The acid solution lead content of cement should be ≤100mg/kg;
7. The soluble fluorine: 24h solubility ≤1.0% ;
8. The remaining teeth or metal surface of the adhesive powder liquid condensation should be promptly wiped with wet cotton ball, otherwise it is not easy to remove ;
9. Reconcile utensil : glass plate and stainless steel knife, smooth surface requirements.
About the dental cement, we have
1,glass ionomer cement for dental permanent luting, cavity liner
2,zinc polycarboxylate cement for dental permanent luting and cavity liner,
3,zinc oxide eugenol cement for temporary luting and cavity liner,
Product feature:
* powder and Liquid: 2.3:1/2.7:1
*Working Time: 45-60seconds
*Net curing time:1.5-6minutes
*Compressive strength: over