Quick Details
-
Application:
-
making mold for detailed reproduction
-
Color:
-
White
-
Hardness:
-
20 Shore A
-
Features:
-
High flowability and long working time
-
Mixing ratio:
-
100:2
-
Advantage:
-
Very low hardness
-
Shrinkage:
-
0.3%
-
Using way:
-
pouring
-
Curing agent:
-
free curing agent
-
HS code:
-
39100000
Quick Details
-
Place of Origin:
-
Guangdong, China
-
Brand Name:
-
DC SILICONE
-
Model Number:
-
DC-C series
-
Application:
-
making mold for detailed reproduction
-
Color:
-
White
-
Hardness:
-
20 Shore A
-
Features:
-
High flowability and long working time
-
Mixing ratio:
-
100:2
-
Advantage:
-
Very low hardness
-
Shrinkage:
-
0.3%
-
Using way:
-
pouring
-
Curing agent:
-
free curing agent
-
HS code:
-
39100000
Tin Cure Silicone for Resin/PU Mold Making RTV-2 Silikon Rubber
1. FEATURES
Outstanding release properties
High flowability and long working time
Very low hardness
High tear resistance High elasticity, for easy removal of complex replica parts
Can be made thixotropic (non-flowable) for vertical surface replication
2. DESCRIPTION SILASTIC
DC-C20 is a two component material consisting of DC-C20 Base, which, when mixed with Curing Agent, cures at room temperature by a condensation reaction. A range of materials can be cast into the cured silicone mould: plaster, polyurethane and polyester resins are materials typically used.
3. APPLICATION
DC-C Series silicone rubber is used for making molds of concrete stone, GRC, gypsum decoration, plaster
ornaments, fiberglass products, polyester decoration, unsaturated resin crafts, polyresin crafts, polyurethane,
bronze, wax, candle, and similar products.
4. TECHNICAL DATASHEET
(DC-C Series with different hardness from 10-40 shore A, different hardness has different application, pls check our suggestion as below for your reference):
DC-C10 and DC-C15 and DC-C20 Silicone rubber are kinds of soft silicone with good fluidity ,its suitable for small size product with detailed pattern by pouring operation, especially popular for the manufacturer of very small resin crafts and candle decorations .
SHELF LIFE
Twelve(12) months when stored under dry and cool place by original package under 25℃.
Package
- small size: 1kg/jar; 5kg/jar; 10kg/jar.
- General size: 20kg/pail; 25kg/pail; 200kg/pail.
Delivery time
- Depends on the express you choose and the destination.
- Via express: general 3-7 business days worlwide.
Shipping cost
- Based on the weight of the goods and the destination.
Tracking number
- The tracking number will be sent to you the next day after shipping.
1. Specialized in rtv2 silicone since 2008
2. Advanced production and R&D equipment, we have two separated production line and equipment
3. Professional R&D team
4. Experienced QC team
5. Professional sales team, fastest response 24 hours full-time service
6. On time delivery, monthly production reaches 200 tons
7. Free sample before order
8. Quality assurance. Each order will be inspected strictly before shipment. We guarantee to our customers: you would get a full refund if there is any quality problem.
9. Professional technical support, both in rtv2 silicone and mould making technology
10. Face- face business talking. We would fly to talk with you only if you have the wil ling of long termbusiness cooperation.
11. Factory visiting anytime
12. All kinds of certificates, such as MSDS
13. Highest performance cost ratio - best quality and reasonable price.
14. Experienced purchasing team to guarantee sufficient raw material
15. DIY service: various size of packages and customized labels
16. Sharing latest industry information
17.Marketing assistance to help you expand your local business
STEP 1: PREPARE THE ORIGINAL MOLDS
- Make your original molds perfect fix it on a board. And fix the original mold on a board , then used four piece of board to enclose the original molds.
STEP2: TAKE 100G PARTS A AND ADD 2G PARTS B, MIX THEM EVENLY. (*NOTES)
- Mold making silicon rubber is a kind of flowing liquid ,it contains two parts. Part A is a kind of flowing white liquid and part B is the curing agent or catalyst .Pls follow the step strictly:
- Weigh the two part exactly by electronic weight. If not, for example add too much catalyst , the operation time will be too fast to operate ,which will cause inconvenience to operate .
- Mix part A and part B evenly. Otherwise the silicon rubber will be partly solidified and this will give birth to difficulties in your final operation. What’s more, the finished molds will meet a short life. All of these will cause a waste of silicon rubber.
STEP 3: VACUUM PUMPING
- Without exception, this step takes less than 10 minutes.Otherwise,it will cause cross linking reaction, and no more further steps will be available.
STEP 4: POURING CASTING OR BRUSH OPERATION? (NOTES)
- For simple pattern products we suggest use pouring operation way, which will be very easy to operate and demould. Pourable silicone require low viscosity which will be easy to flow smoothly and easy to de-air .
- For delicate pattern products we suggest use brushing operation way, which can copy the pattern exactly . Brushable silicone require high viscosity which won ’t be easy to flow away and easy to brush .
- We sugges to set the silicone mold for another 12 hours after demould before you put it into a large production .
*WARM TIPS
As addition cure silicone is a kind of platinum cure system, which will be easy to cause uncured problem , so pls kindly follow the tips as below :
- Do not mix with liquid condensation silicone rubber or even the tool which used for condensation silicone rubber.
- Do not mix with organic matter which contains N, S, P organics and ionic compound like Sn, As,Hg, Ph. (Do not smoke when you use this addition silicone rubber)
- Do not add any pigment or powder into the addition cure silicone rubber without any testing to prevent uncured problem.