PPA compound, 35% glass fiber reinforced, heat stabilized. Intended for engineering applications that require a maximum service temperature higher than that of normal aliphatic polyamides. In addition to the outstanding thermal and chemical resistance, it provides high and constant mechanical performance, unaltered even after moisture absorption. Excellent creep behavior and dimensional stability. Extended heat ageing resistance.
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | 60x60x2; ISO 294-4 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | 60x60x2; ISO 294-4 |
| Melt Flow |
25 g/10 min
@Load 10.0 kg, Temperature 220 °C |
25 g/10 min
@Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 90.0 MPa | 13100 psi | ISO 2039-1 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | >= 15 % | >= 15 % | 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 2.4 % | 2.4 % | 50 mm/min; ISO 527-1, -2 |
| Tensile Modulus | 2.20 GPa | 319 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 62.0 MPa | 8990 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.10 GPa | 305 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) |
12.0 kJ/m²
@Temperature -30.0 °C |
5.71 ft-lb/in²
@Temperature -22.0 °F |
ISO 180-1A |
|
23.0 kJ/m²
@Temperature 23.0 °C |
10.9 ft-lb/in²
@Temperature 73.4 °F |
ISO 180-1A | |
| Charpy Impact Unnotched |
15.0 J/cm²
@Temperature -30.0 °C |
71.4 ft-lb/in²
@Temperature -22.0 °F |
ISO 179-1eU |
|
NB
@Temperature 23.0 °C |
NB
@Temperature 73.4 °F |
ISO 179-1eU | |
| Charpy Impact, Notched |
1.40 J/cm²
@Temperature -30.0 °C |
6.66 ft-lb/in²
@Temperature -22.0 °F |
ISO 179-1eA |
|
2.40 J/cm²
@Temperature 23.0 °C |
11.4 ft-lb/in²
@Temperature 73.4 °F |
ISO 179-1eA | |