High temperature resistant for resin or epoxy molds silicone rubber platinum cure liquid silicone rubber

FOB Reference Price: Get Latest Price

≥1 Kilograms

US $4.9

Free Inquiry

Customized Request

Quick Details

Products Description

Additive Mold silicone

Additive mold silicone is usually called two-component room temperature vulcanization molding silicone. The A and B components of

the silicone are liquid, containing platinum thixotropy, catalyst or other additives, and can be cured at room temperature or at

elevated temperature after mixing.

* Metal crafts, alloy car and other precision mold manufacturing

* Molding of epoxy resin, polyester resin, polystyrene, vinyl plastic, paraffin, etc.

* Manufacture of molds for large cement components, cultural stones, concrete and other products

* Design and production of high-precision hand-plate models, automotive development, power airfoil

* Food grade mold making

* Customized Product

Product Paramenters

Model	H615	H620	H625	H630	H640	H650	H660
Appearance	Translucent	Translucent	Translucent	Translucent	Translucent	Translucent	Off-white
Hardness (Shore Aº)	15±2	20±2	25±2	30±2	40±2	50±2	60±2
Two components mixed weight ratio (A: B)	1:1	1:1	1:1	1:1	1:1	1:1	1:1
Dynamic viscosity (mPa.s)	4000±2000	5000±2000	6000±2000	7000±2000	8000±2000	9000±2000	10000±2000
Tensile strength (MPa)	4.6	5.6	6.2	6.2	6.8	4.3	4.2
Tear strength(kN/m)	18±2	25±2	25±2	25±2	27±2	15±2	12±2
Elongation (%)	530	560	600	600	680	270	190
Density(g/cm)	1.05	1.05	1.07	1.13	1.14	1.16	1.18
Operation time(min)	30-60	30-60	30-60	30-60	30-60	30-60	30-60
Vulcanization time (h)	4-6	4-6	4-6	4-6	4-6	4-6	4-6
Line shrinkage not rate (%)	≤0.1	≤0.1	≤0.1	≤0.1	≤0.1	≤0.1	≤0.1

Model	T615	T620	T625	T630	T640	T650	T660
Appearance	Transparent	Transparent	Transparent	Transparent	Transparent	Transparent	Off-white
Hardness (Shore Aº)	15±2	20±2	25±2	30±2	40±2	50±2	60±2
Two components mixed weight ratio (A: B)	1:1	1:1	1:1	1:1	1:1	1:1	1:1
Dynamic viscosity (mPa.s)	80000±2000	80000±2000	260000±2000	260000±2000	260000±2000	260000±2000	260000±2000
Tensile strength (MPa)	4.8	5.9	6.2	6.2	6.8	4.3	4.2
Tear strength(kN/m)	15±2	18±2	20±2	20±2	20±2	15±2	12±2
Elongation (%)	380	380	400	420	420	270	190
Density(g/cm)	1.05	1.05	1.07	1.13	1.14	1.16	1.18
Operation time(min)	30-60	30-60	30-60	30-60	30-60	30-60	30-60
Vulcanization time (h)	8-10	8-10	8-10	8-10	8-10	8-10	8-10
Line shrinkage not rate (%)	≤0.1	≤0.1	≤0.1	≤0.1	≤0.1	≤0.1	≤0.1