- Product Details
- {{item.text}}
Quick Details
-
CaO Content (%):
-
0.5%
-
CrO Content (%):
-
0
-
SiC Content (%):
-
98%
-
Place of Origin:
-
Hebei, China
-
Model Number:
-
zq0918
-
Brand Name:
-
YUTONG
-
Density:
-
3.0g/cm3
-
Bending Strength at High Temperature:
-
250 Mpa
-
Application scenarios:
-
Industrial Furnaces
-
Color:
-
Black Grey
-
Raw material:
-
Silicon Carbide
-
Thermal conductivity(w/mk):
-
45W/MK(1200 )
-
Type:
-
Facotory
-
Product name:
-
silicon carbide square beam
Quick Details
-
SiO2 Content (%):
-
International Standard
-
Al2O3 Content (%):
-
0
-
MgO Content (%):
-
0
-
CaO Content (%):
-
0.5%
-
CrO Content (%):
-
0
-
SiC Content (%):
-
98%
-
Place of Origin:
-
Hebei, China
-
Model Number:
-
zq0918
-
Brand Name:
-
YUTONG
-
Density:
-
3.0g/cm3
-
Bending Strength at High Temperature:
-
250 Mpa
-
Application scenarios:
-
Industrial Furnaces
-
Color:
-
Black Grey
-
Raw material:
-
Silicon Carbide
-
Thermal conductivity(w/mk):
-
45W/MK(1200 )
-
Type:
-
Facotory
-
Product name:
-
silicon carbide square beam
Reaction Sintered Silicon Carbide beam is used for the loading structure systems of tunnel kiln, shuttle kiln and other industry furnaces.It features high strength,high hardness, high wear resistance, corrosion resistance, good oxidation resistance, thermal shock resistance. It is an ideal kiln furniture for sanitary ware and electric porcelain industry, its good thermal conductivity performance can reduce energy consumption without increasing the weight of kiln car.
This beam frame can increase the loading capacity, reduce gas and electricity consuming, shorten the firing time.
Silicon Carbide Lines that we can supply:
1. Reaction Sintered Silicon carbide (RBSIC)
2. Recrystallized Silicon Carbide ceramic (RS I C)
3. Nitride Bonded Silicon Carbide ceramic (NS I C)
4. Oxide Silicon Carbide ( O SiC)
Technical Data Sheet for RBSIC
|
I tems |
U nit |
Index |
|
Max.Service Temp |
℃ |
1380 |
|
Density |
g/cm 3 |
3.02 |
|
Porosity |
% |
<0.1 |
|
Bending Strength |
Mpa |
250(20℃) |
|
Mpa |
280(1200℃) |
|
|
Modulus Strength |
Gpa |
330(20℃) |
|
Gpa |
300(1200℃) |
|
|
Thermal conductivity |
W/m.k |
45(1200℃) |
|
Thermal Expansion |
K- 1 x10- 6 |
4.5 |
|
Vickers-hardness |
Gpa |
20 |
|
Acid-proof alkaline |
|
EXCELLENT |