For repair of hole and crack of iron castings. Can be used to repair finishining matching surface and restore of size erros. Wear resistance, corrosion resistance, almost same color to the parts after repair. Can be lated, milled, grinded, drilled after curing.
- Product Details
- {{item.text}}
Quick Details
-
EINECS No.:
-
38891-59-7
-
Place of Origin:
-
Jiangxi, China
-
Brand Name:
-
HiGlue
-
Model Number:
-
111 112 113
-
Type:
-
Epoxy Iron Repair, Epoxy Iron Repair
-
Application:
-
Fast Fix
-
Shelf life:
-
12 Months
-
Ratio:
-
4(A):1(B)
-
Model:
-
Iron,steel,aluminium,copper
-
Tensile strength(Mpa):
-
39
-
Compressive strength (Mpa):
-
125
-
shear strength(Mpa):
-
19
-
Hardness:
-
80
-
deliver time:
-
3-7 working days
Quick Details
-
CAS No.:
-
38891-59-7
-
Other Names:
-
Iron Putty
-
MF:
-
C21H23CIFNO2
-
EINECS No.:
-
38891-59-7
-
Place of Origin:
-
Jiangxi, China
-
Brand Name:
-
HiGlue
-
Model Number:
-
111 112 113
-
Type:
-
Epoxy Iron Repair, Epoxy Iron Repair
-
Application:
-
Fast Fix
-
Shelf life:
-
12 Months
-
Ratio:
-
4(A):1(B)
-
Model:
-
Iron,steel,aluminium,copper
-
Tensile strength(Mpa):
-
39
-
Compressive strength (Mpa):
-
125
-
shear strength(Mpa):
-
19
-
Hardness:
-
80
-
deliver time:
-
3-7 working days
Product Description
HiGlue Metal Repair Epoxy Putty
are high performance metal-filled epoxies. They are the best choice for repairing air holes, sand holes, cracks in casting parts. Also, can patch not-structural defect. Quickly make the worn equipment return to service with cost efficiency.
Features
• Metal-filled two-component epoxy putty;
• Bonds to metals, concrete and plastics;
• Cures at room temperature;
• High strength, Can be drilled, tapped, machined or painted;
• Excellent resistance to oil, gasoline, water and chemicals;
• Ideal for patching and repairing areas where welding or brazing is undesirable.
•
Rebuild and repair various steel material imperfect, crackle and wearing.
•
Wear and corrosion resistance, no shrinkage, similar to original material colors.
•
Working temperature: -60°C~+160°C.
•
Shelf Life: 12 months
Technical Information
|
Product Name
|
111
|
|
Package size
|
500g
|
|
Mix ration
|
4(A):1(B)
|
|
Typical applications
|
High performance cast iron repairing agent
|
|
Compressive strength
|
125Mpa
|
|
Hardness
|
80
|
|
Working temperature
|
-50°C~160°C
|
2.Model
HiGlue 111 Iron Putty
HiGlue 112 Steel Putty
Applicable for repairing a variety of carbon steel, alloy steel, stainless steel. For bug fixes, component wear, scratches, corrosion and fracture. Wear and corrosion resistance, high strength. Can be lated, milled, grinded, drilled after curing.
HiGlue 113 Aluminum Putty
Applicable for repairing all kinds of aluminum materials and aluminum casting holes, sand holes, shrinkage and other bug fixes as well as scratches, cracks and wear patches. Wear and corrosion resistance. Almost same color to the parts after repair, Can be lated, milled, grinded, drilled after curing.
|
Model
|
Useage
|
Weight
Rate
|
VolumeRatio
|
Compressive Strength
|
Tensile Strength
|
Shear Strength
|
Bending Strength
|
Shore D
|
Working Temperature
|
|
HG111
|
Iron putty
|
7:1
|
4:1
|
125Mpa
|
42Mpa
|
20Mpa
|
78Mpa
|
82
|
-60°C~+160°C
|
|
HG112
|
Steel putty
|
7:1
|
4:1
|
106.5Mpa
|
35Mpa
|
19Mpa
|
58Mpa
|
80
|
-50°C~+160°C
|
|
HG113
|
Aluminum Putty
|
6:1
|
4.5:1
|
99.6Mpa
|
41Mpa
|
20Mpa
|
55Mpa
|
80
|
-50°C~+160°C
|
Application
Areas of Application:
Mainly apply in filling the air holes and sand holes, sealing the cracks, also, can patch not-structural defects.
Repairs cracks, dents and breaks in stainless steel equipment, machinery or castings.
Rebuilds dairy equipment Repairs stainless steel holding tanks.
Repairs cracks, dents and breaks in stainless steel equipment, machinery or castings.
Rebuilds dairy equipment Repairs stainless steel holding tanks.
How to use
★ Surface treatment: surface treatment has a great influence on the repair effect. By repairing the surface should be polished rough or sandblasting processing, to grind the base material color, special treatment for some special conditions, such as cast iron pump shell surface rust water zone to the moisture within the surface using the method of flame barbecue shaved, then polished or sandblasting: class for some shaft or hole wear size, on the premise of ensure enough strength, can be polished or turning threads of the rough surface. Rectangular groove or dovetail groove should be polished at the scratched part of the guide
rail or cylinder block, and the depth should be more than 2mm.
★ Cleaning: with cleaning agent or absorbent cotton dipped in acetone cleaning polished surface to remove residual oil.
★ Mixed repair putty: repair putty is composed of A and B two components, the use of strictly in accordance with the provisions of the mixing ratio of A and B components fully mixed, according to the quality ratio A:B = 2:1 or volume ratio A:B = 2:1. Use it up within the specified operable time limit. If the prepared glue is not used up at one time, the remaining glue cannot be used again. It is suggested to use it along with it to reduce waste.
★ Glue: with the scraper or glue knife will be mixed with good repair putty coated on the surface to repair, can be coated with a little, with the scraper or glue knife repeatedly pressed, so that the repair putty and matrix fully infiltrated filling, and then coated with the rest of the repair putty, set aside enough for processing, or using molding method.
★ Curing: under normal conditions at room temperature (20~25℃) curing for 8 hours can be machined, 24 hours can be put into use; When the temperature is below 25℃, the curing time is appropriately extended. When the temperature of the surface to be repaired is below 15℃, the proper heating method must be adopted to ensure the curing of the coating.
rail or cylinder block, and the depth should be more than 2mm.
★ Cleaning: with cleaning agent or absorbent cotton dipped in acetone cleaning polished surface to remove residual oil.
★ Mixed repair putty: repair putty is composed of A and B two components, the use of strictly in accordance with the provisions of the mixing ratio of A and B components fully mixed, according to the quality ratio A:B = 2:1 or volume ratio A:B = 2:1. Use it up within the specified operable time limit. If the prepared glue is not used up at one time, the remaining glue cannot be used again. It is suggested to use it along with it to reduce waste.
★ Glue: with the scraper or glue knife will be mixed with good repair putty coated on the surface to repair, can be coated with a little, with the scraper or glue knife repeatedly pressed, so that the repair putty and matrix fully infiltrated filling, and then coated with the rest of the repair putty, set aside enough for processing, or using molding method.
★ Curing: under normal conditions at room temperature (20~25℃) curing for 8 hours can be machined, 24 hours can be put into use; When the temperature is below 25℃, the curing time is appropriately extended. When the temperature of the surface to be repaired is below 15℃, the proper heating method must be adopted to ensure the curing of the coating.
Packing & Shipping
HiGlue 111: 500g/set; 15set/ carton, carton size:
52*33*15.5cm;
HiGlue 112: 500g/set; 15set/ carton,
carton size: 52*33*15.5cm;
HiGlue 113: 250g/set; 15set/ carton,
carton size: 52*33*15.5cm.
Our Certifications
Our Company
Jiangxi Gooz Adhesive Co., Ltd
Our company is an innovative enterprise based on research and development, production and marketing.
The over 20 years of experience helps us take a leading position in the industry and we have won great reputations from customers
all over the world.
all over the world.
1. HiGlue liquid thread locker: 222 242 243 262 270 271 272 277 290 326
2. HiGlue pipe thread sealant: 545 554 565 567 569 577 542 561 L55
3. HiGlue instant super glue: 401 403 406 407 410 411 412 414 415 454 460 480 495 496
4. HiGlue flange/ plane sealant: 510 515 518 5182 5208 573 574
5. HiGlue silicone rubber: 207 587 593 594 595 596 598 5020 5699 5900 5910 5920
6. HiGlue retaining compound: 603 6050 609 620 638 641 648 6482 660 661 662 680 6001
7. HiGlue surface treatment: 7075 7452 7649 7387 7471 770 754 790
8. HiGlue Metal Epoxy Putty: 111 112 113 114
9. HiGlue Epoxy Tile Grout And Epoxy Anchor
10. HiGlue wear guard high load 11490/11470/9313
2. HiGlue pipe thread sealant: 545 554 565 567 569 577 542 561 L55
3. HiGlue instant super glue: 401 403 406 407 410 411 412 414 415 454 460 480 495 496
4. HiGlue flange/ plane sealant: 510 515 518 5182 5208 573 574
5. HiGlue silicone rubber: 207 587 593 594 595 596 598 5020 5699 5900 5910 5920
6. HiGlue retaining compound: 603 6050 609 620 638 641 648 6482 660 661 662 680 6001
7. HiGlue surface treatment: 7075 7452 7649 7387 7471 770 754 790
8. HiGlue Metal Epoxy Putty: 111 112 113 114
9. HiGlue Epoxy Tile Grout And Epoxy Anchor
10. HiGlue wear guard high load 11490/11470/9313
Hot Searches